We report on the performance of AlGaN-based deep ultraviolet light-emitting diodes(UV-LEDs)emitting at 265 nm grown on stripe-patterned high-temperature annealed(HTA)epitaxially laterally overgrown(ELO)aluminium nitri...We report on the performance of AlGaN-based deep ultraviolet light-emitting diodes(UV-LEDs)emitting at 265 nm grown on stripe-patterned high-temperature annealed(HTA)epitaxially laterally overgrown(ELO)aluminium nitride(AIN)/sapphire templates.For this purpose,the structural and electro-optical properties of ultraviolet-c light-emitting diodes(UVC-LEDs)on as-grown and on HTA planar AlN/sapphire as well as ELO AlN/sapphire with and without HTA are investigated and compared.Cathodoluminescence measurements reveal dark spot densities of 3.5×10^9 cm^-2,1.1×10^9 cm^-2,1.4×10^9 cm^-2,and 0.9×10^9 cm^-2 in multiple quantum well samples on as-grown planar AIN/sapphire,HTA planar AlN/sapphire,ELO AlN/sapphire,and HTA ELO AlN/sapphire,respectively,and are consistent with the threading dislocation densities determined by transmission electron microscopy(TEM)and high-resolution X-ray diffraction rocking curve.The UVC-LED performance improves with the reduction of the threading dislocation densities(TDDs).The output powers(measured on-wafer in cw operation at 20 mA)of the UV-LEDs emitting at 265 nm were 0.03 mW(planar AlN/sapphire),0.8 mW(planar HTA AlN/sapphire),0.9 mW(ELO AlN/sapphire),and 1.1 mW(HTA ELO AlN/sapphire),respectively.Furthermore,Monte Carlo ray-tracing simulations showed a 15%increase in light-extraction efficiency due to the voids formed in the ELO process.These results demonstrate that HTA ELO AlN/sapphire templates provide a viable approach to increase the efficiency of UV-LEDs,improving both the internal quantum efficiency and the light-extraction efficiency.展开更多
We report on AlGaN-based tunnel heterojunctions grown by metalorganic vapor phase epitaxy enabling fully transparent UVC LEDs by eliminating the absorbing p-AlGaN and p-GaN layers. Furthermore, the electrical characte...We report on AlGaN-based tunnel heterojunctions grown by metalorganic vapor phase epitaxy enabling fully transparent UVC LEDs by eliminating the absorbing p-AlGaN and p-GaN layers. Furthermore, the electrical characteristics can be improved by exploiting the higher conductivity of n-AlGaN layers as well as a lower resistance of n-contacts. UVC LEDs with AlGaN:Mg/AlGaN:Si tunnel junctions exhibiting single peak emission at268 nm have been realized, demonstrating effective carrier injection into the AlGaN multiple quantum well active region. The incorporation of a low band gap interlayer enables effective tunneling and strong voltage reduction.Therefore, the interlayer thickness is systematically varied. Tunnel heterojunction LEDs with an 8 nm thick GaN interlayer exhibit continuous-wave emission powers >3 m W near thermal rollover. External quantum efficiencies of 1.4% at a DC current of 5 m A and operating voltages of 20 V are measured on-wafer. Laterally homogeneous emission is demonstrated by UV-sensitive electroluminescence microscopy images. The complete UVC LED heterostructure is grown in a single epitaxy process including in situ activation of the magnesium acceptors.展开更多
基金Bundesministerium für Bildung und Forschung(03ZZ0134C,Advanced UV for Life)Deutsche Forschungsgemeinschaft(Semiconductor Nanophotonics,Collaborative Research Centre,CRC7879315)。
文摘We report on the performance of AlGaN-based deep ultraviolet light-emitting diodes(UV-LEDs)emitting at 265 nm grown on stripe-patterned high-temperature annealed(HTA)epitaxially laterally overgrown(ELO)aluminium nitride(AIN)/sapphire templates.For this purpose,the structural and electro-optical properties of ultraviolet-c light-emitting diodes(UVC-LEDs)on as-grown and on HTA planar AlN/sapphire as well as ELO AlN/sapphire with and without HTA are investigated and compared.Cathodoluminescence measurements reveal dark spot densities of 3.5×10^9 cm^-2,1.1×10^9 cm^-2,1.4×10^9 cm^-2,and 0.9×10^9 cm^-2 in multiple quantum well samples on as-grown planar AIN/sapphire,HTA planar AlN/sapphire,ELO AlN/sapphire,and HTA ELO AlN/sapphire,respectively,and are consistent with the threading dislocation densities determined by transmission electron microscopy(TEM)and high-resolution X-ray diffraction rocking curve.The UVC-LED performance improves with the reduction of the threading dislocation densities(TDDs).The output powers(measured on-wafer in cw operation at 20 mA)of the UV-LEDs emitting at 265 nm were 0.03 mW(planar AlN/sapphire),0.8 mW(planar HTA AlN/sapphire),0.9 mW(ELO AlN/sapphire),and 1.1 mW(HTA ELO AlN/sapphire),respectively.Furthermore,Monte Carlo ray-tracing simulations showed a 15%increase in light-extraction efficiency due to the voids formed in the ELO process.These results demonstrate that HTA ELO AlN/sapphire templates provide a viable approach to increase the efficiency of UV-LEDs,improving both the internal quantum efficiency and the light-extraction efficiency.
基金Bundesministerium für Bildung und Forschung(BMBF)“Advanced UV for Life” Project(03ZZ0134C)Deutsche Forschungsgemeinschaft(DFG)Collaborative Research Centre “Semiconductor Nanophotonics”(CRC787 9315)
文摘We report on AlGaN-based tunnel heterojunctions grown by metalorganic vapor phase epitaxy enabling fully transparent UVC LEDs by eliminating the absorbing p-AlGaN and p-GaN layers. Furthermore, the electrical characteristics can be improved by exploiting the higher conductivity of n-AlGaN layers as well as a lower resistance of n-contacts. UVC LEDs with AlGaN:Mg/AlGaN:Si tunnel junctions exhibiting single peak emission at268 nm have been realized, demonstrating effective carrier injection into the AlGaN multiple quantum well active region. The incorporation of a low band gap interlayer enables effective tunneling and strong voltage reduction.Therefore, the interlayer thickness is systematically varied. Tunnel heterojunction LEDs with an 8 nm thick GaN interlayer exhibit continuous-wave emission powers >3 m W near thermal rollover. External quantum efficiencies of 1.4% at a DC current of 5 m A and operating voltages of 20 V are measured on-wafer. Laterally homogeneous emission is demonstrated by UV-sensitive electroluminescence microscopy images. The complete UVC LED heterostructure is grown in a single epitaxy process including in situ activation of the magnesium acceptors.