The molecular weight distributions were estimated for carbon fiber polymer precursors such as poly（acrylonitrile-co-itaconic acid） synthesized by semi batch solution polymerization in mixed solvents media with the a...The molecular weight distributions were estimated for carbon fiber polymer precursors such as poly（acrylonitrile-co-itaconic acid） synthesized by semi batch solution polymerization in mixed solvents media with the azonitrile compounds as initiator under the different ratios of solvent and non solvent from 0.75 to 2.5 in weight. The copolymer was characterized by using Fourier transform infrared spectroscopy （FTIR） and nuclear magnetic resonance （1H-NMR） analyses. The molecular weight distributions were evaluated by Mv/Mn ratios estimated from viscosity and osmotic measurements, and Mw/Mn estimated from size exclusion chromatography. The molecular weight distributions of these polymers as determined from M, JMn and Mw/Mn are 2.9 to 3,2 and 2.0 to 2.5 respectively. The molecular distributions were close to a narrow distribution of 2.0 when the solvent/non-solvent ratio was varied between 1.4 and 2.0. Intrinsic viscosity [η] as a function of molecular weight of poly（acrylonitrile-co-itaconic acid） was evaluated by means of low angle laser light scattering with size exclusion chromatography （SEC-LALLS） and viscometry with SEC （SEC-VISCO）. The relationship between [η] and Mw for poly（acrylonitrile-co-itaconic acid） in DMF at 50℃ was [q] = 1.1×10-5 Mw0.79, where [η] is obtained in dL/g.展开更多
基金financially supported by the Council of Scientific and Industrial Research,New Delhi under Supra Institutional Project(SIP-IFCAP-04)
文摘The molecular weight distributions were estimated for carbon fiber polymer precursors such as poly（acrylonitrile-co-itaconic acid） synthesized by semi batch solution polymerization in mixed solvents media with the azonitrile compounds as initiator under the different ratios of solvent and non solvent from 0.75 to 2.5 in weight. The copolymer was characterized by using Fourier transform infrared spectroscopy （FTIR） and nuclear magnetic resonance （1H-NMR） analyses. The molecular weight distributions were evaluated by Mv/Mn ratios estimated from viscosity and osmotic measurements, and Mw/Mn estimated from size exclusion chromatography. The molecular weight distributions of these polymers as determined from M, JMn and Mw/Mn are 2.9 to 3,2 and 2.0 to 2.5 respectively. The molecular distributions were close to a narrow distribution of 2.0 when the solvent/non-solvent ratio was varied between 1.4 and 2.0. Intrinsic viscosity [η] as a function of molecular weight of poly（acrylonitrile-co-itaconic acid） was evaluated by means of low angle laser light scattering with size exclusion chromatography （SEC-LALLS） and viscometry with SEC （SEC-VISCO）. The relationship between [η] and Mw for poly（acrylonitrile-co-itaconic acid） in DMF at 50℃ was [q] = 1.1×10-5 Mw0.79, where [η] is obtained in dL/g.