β-A13Mg2 intermetallic was used as a reinforcing agent to improve the mechanical properties of an aluminum matrix. Different amounts of A13Mg2 nanoparticles （ranging from 0wt% to 20wt%） were milled with aluminum po...β-A13Mg2 intermetallic was used as a reinforcing agent to improve the mechanical properties of an aluminum matrix. Different amounts of A13Mg2 nanoparticles （ranging from 0wt% to 20wt%） were milled with aluminum powders in a planetary ball mill for 10 h. Consolidation was conducted by uniaxial pressing at 400β under a pressure of 600 MPa for 2 h. Microstructural characterization confirms the uniform distribution of A13Mg2 nanoparticles within the matrix. The effects of nano-sized A13Mg2 content on the wear and mechanical properties of the composites were also investigated. The results show that as the A13Mg2 content increases to higher levels, the hardness, compressive strength, and wear resistance of the nanocomposites increase significantly, whereas the relative density and ductility decrease. Scanning electron microscopy （SEM） analysis of worn surfaces reveals that a transition in wear mechanisms occurs from delamination to abrasive wear by the addition of A13Mg2 nanoparticles to the matrix.展开更多
基金Iran National Science Foundation,Universities of Tehran and Tabriz (Sahand University of Technology) for financial support
文摘β-A13Mg2 intermetallic was used as a reinforcing agent to improve the mechanical properties of an aluminum matrix. Different amounts of A13Mg2 nanoparticles （ranging from 0wt% to 20wt%） were milled with aluminum powders in a planetary ball mill for 10 h. Consolidation was conducted by uniaxial pressing at 400β under a pressure of 600 MPa for 2 h. Microstructural characterization confirms the uniform distribution of A13Mg2 nanoparticles within the matrix. The effects of nano-sized A13Mg2 content on the wear and mechanical properties of the composites were also investigated. The results show that as the A13Mg2 content increases to higher levels, the hardness, compressive strength, and wear resistance of the nanocomposites increase significantly, whereas the relative density and ductility decrease. Scanning electron microscopy （SEM） analysis of worn surfaces reveals that a transition in wear mechanisms occurs from delamination to abrasive wear by the addition of A13Mg2 nanoparticles to the matrix.