Composite resin restorations are routinely exposed to acidic and chromogenic beverages that may alter their surface integrity over time.This in-vitro study evaluated the surface roughness behavior of two universal sin...Composite resin restorations are routinely exposed to acidic and chromogenic beverages that may alter their surface integrity over time.This in-vitro study evaluated the surface roughness behavior of two universal single-shade(Unishade)composites and two conventionalmulti-shade composites following immersion in commonly consumed staining solutions and assessed whether repolishing could restore smoothness after degradation.A total of 120 standardized disc specimens were fabricated and allocated to fourmaterial groups,with each group subdivided into distilled water,cola,and coffee immersion subgroups.Surface roughness was recorded at baseline,after one week,after one month,and following a final repolishing step using a standardized multi-step system.The findings demonstrated that Unishade composites exhibited more stable surface characteristics across all immersion periods,with changes consistently remaining below the threshold associated with biofilm accumulation.Conventional composites showed greater variability,particularly in cola,where roughness values increased significantly compared with distilled water and coffee.Repolishing substantially reduced immersion-induced roughness in all materials,although its effectiveness varied depending on composite formulation and beverage acidity.Cola produced the greatest surface alterations across all groups,highlighting the erosive potential of low-pH beverages.These results indicate that Unishade composites possess superior resistance to surface degradation,likely due to their nano-structured filler configuration and less hydrophilic resin matrices,while conventional materials appear more susceptible to acidic challenge.Within the limitations of this study,selecting surface-stable material types and applying appropriate finishing and repolishing protocols may enhance the long-term performance and esthetics of composite restorations.展开更多
文摘Composite resin restorations are routinely exposed to acidic and chromogenic beverages that may alter their surface integrity over time.This in-vitro study evaluated the surface roughness behavior of two universal single-shade(Unishade)composites and two conventionalmulti-shade composites following immersion in commonly consumed staining solutions and assessed whether repolishing could restore smoothness after degradation.A total of 120 standardized disc specimens were fabricated and allocated to fourmaterial groups,with each group subdivided into distilled water,cola,and coffee immersion subgroups.Surface roughness was recorded at baseline,after one week,after one month,and following a final repolishing step using a standardized multi-step system.The findings demonstrated that Unishade composites exhibited more stable surface characteristics across all immersion periods,with changes consistently remaining below the threshold associated with biofilm accumulation.Conventional composites showed greater variability,particularly in cola,where roughness values increased significantly compared with distilled water and coffee.Repolishing substantially reduced immersion-induced roughness in all materials,although its effectiveness varied depending on composite formulation and beverage acidity.Cola produced the greatest surface alterations across all groups,highlighting the erosive potential of low-pH beverages.These results indicate that Unishade composites possess superior resistance to surface degradation,likely due to their nano-structured filler configuration and less hydrophilic resin matrices,while conventional materials appear more susceptible to acidic challenge.Within the limitations of this study,selecting surface-stable material types and applying appropriate finishing and repolishing protocols may enhance the long-term performance and esthetics of composite restorations.
