The influences of hyperbranched polyethylenimine （hPEI）, which possesses many reactive amino end-groups, on the blending properties of bisphenol-A polycarbonate （PC） and amorphous polyamide （aPA） were systematic...The influences of hyperbranched polyethylenimine （hPEI）, which possesses many reactive amino end-groups, on the blending properties of bisphenol-A polycarbonate （PC） and amorphous polyamide （aPA） were systematically investigated. Scanning electron microscopy （SEM） and differential scanning calorimetry （DSC） were used to observe the effect of hPE1 on morphologies of PC and aPA phases in bulk blends. While the interfacial fracture toughness between planar PC and aPA layers with and without hPEI was studied by using augmented double cantilever beam （ADCB） method. Results show that the compatibility in PC/aPA blends can be significantly improved by adding a small amount of hPEI, mainly due to the interchange reactions between the polymers leading to the formation of block copolymers, cross-linked polymers and molecules with other constitutions. The augmented double cantilever beam experiments showed that the reactive process drastically reinforced the interfacial adhesion between planar layers of PC and aPA. However, degradation takes place during annealing at 180℃, which was responsible for the production of small molar mass species of PC.展开更多
基金financially supported by the National Natural Science Foundation of China(No.21004069)
文摘The influences of hyperbranched polyethylenimine （hPEI）, which possesses many reactive amino end-groups, on the blending properties of bisphenol-A polycarbonate （PC） and amorphous polyamide （aPA） were systematically investigated. Scanning electron microscopy （SEM） and differential scanning calorimetry （DSC） were used to observe the effect of hPE1 on morphologies of PC and aPA phases in bulk blends. While the interfacial fracture toughness between planar PC and aPA layers with and without hPEI was studied by using augmented double cantilever beam （ADCB） method. Results show that the compatibility in PC/aPA blends can be significantly improved by adding a small amount of hPEI, mainly due to the interchange reactions between the polymers leading to the formation of block copolymers, cross-linked polymers and molecules with other constitutions. The augmented double cantilever beam experiments showed that the reactive process drastically reinforced the interfacial adhesion between planar layers of PC and aPA. However, degradation takes place during annealing at 180℃, which was responsible for the production of small molar mass species of PC.