The corrosion behavior of 304LN austenitic stainless steel in supercritical CO_(2) at 650℃ was investigated.The results show that 304LN follows Wagner’s law kinetics,forming a protective oxide flm consisting of SiO_...The corrosion behavior of 304LN austenitic stainless steel in supercritical CO_(2) at 650℃ was investigated.The results show that 304LN follows Wagner’s law kinetics,forming a protective oxide flm consisting of SiO_(2),(Cr,Mn)3O_(4),and Cr2O_(3) from the inner to outer layers.A shallow carburization depth of approximately 130 nm indicates excellent resistance to carburization.The roles of key elements in 18/8 austenitic stainless steel represented by 304LN,such as Cr,Ni,and Si,were analyzed,highlighting their contributions to anti-carburization performance and corrosion resistance under harsh conditions.展开更多
基金supported by the Strategic Priority Research Program of the Chinese Academy of Sciences(Grant No.XDA0410000)the CAS Project for Young Scientists in Basic Research(No.YSBR-043)+1 种基金the CNNC Science Fund for Talented Young Scholars,the National Funding Program for Postdoctoral Researchers(GZC20232747)the Youth Innovation Promotion Association CAS(2022187).
文摘The corrosion behavior of 304LN austenitic stainless steel in supercritical CO_(2) at 650℃ was investigated.The results show that 304LN follows Wagner’s law kinetics,forming a protective oxide flm consisting of SiO_(2),(Cr,Mn)3O_(4),and Cr2O_(3) from the inner to outer layers.A shallow carburization depth of approximately 130 nm indicates excellent resistance to carburization.The roles of key elements in 18/8 austenitic stainless steel represented by 304LN,such as Cr,Ni,and Si,were analyzed,highlighting their contributions to anti-carburization performance and corrosion resistance under harsh conditions.