In this article,graphene oxide(GO)and benzotriazole-loaded mesoporous silica nanoparticles(BTA/MSNs)are combined on micro scale through the in situ polymerization of polydopamine(PDA),preparing a selfhealing bi-functi...In this article,graphene oxide(GO)and benzotriazole-loaded mesoporous silica nanoparticles(BTA/MSNs)are combined on micro scale through the in situ polymerization of polydopamine(PDA),preparing a selfhealing bi-functional GO(fGO)used as nano-fillers for anti-corrosion enhancement of waterborne epoxy(WEP)coatings.Scanning electronic microscopy(SEM)images show that the BTA/MSNs are uniformly distributed on the surface of high aspect ratio GO nanosheets to endow GO nanocontainer characteristics.UV-vis profiles demonstrate that fGO has p H-controlled release function.Modulus at lowest frequency is generally used for comparing the corrosion resistance of organic coatings.Modulus at lowest frequency(1.42×10^(5)Ωcm^(2))after 30 days immersion in 3.5 wt.%Na Cl solution revealed 2 orders of magnitude higher that of blank WEP(1.17×10^(7)Ωcm^(2)).With artificial cracks on its coatings,fGO/WEP had no obvious rust compared with blank WEP after 240 h of immersion.We anticipate that self-healing and physical barrier bi-functional nanocontainers improve the traditional anticorrosion coating efficiency with better,longer-lasting performance for shipping,oil drilling or bridge maintenance.展开更多
基金supported by the National Natural Science Foundation of China(Grant No.51908031)the China Scholarship Council for a graduate fellowship(201906150013)+2 种基金the support from Guangdong Special Support Program(Grant No.2017TX04N371)ERC Enercapsule project(647969)Royal Society project IECR2202163。
文摘In this article,graphene oxide(GO)and benzotriazole-loaded mesoporous silica nanoparticles(BTA/MSNs)are combined on micro scale through the in situ polymerization of polydopamine(PDA),preparing a selfhealing bi-functional GO(fGO)used as nano-fillers for anti-corrosion enhancement of waterborne epoxy(WEP)coatings.Scanning electronic microscopy(SEM)images show that the BTA/MSNs are uniformly distributed on the surface of high aspect ratio GO nanosheets to endow GO nanocontainer characteristics.UV-vis profiles demonstrate that fGO has p H-controlled release function.Modulus at lowest frequency is generally used for comparing the corrosion resistance of organic coatings.Modulus at lowest frequency(1.42×10^(5)Ωcm^(2))after 30 days immersion in 3.5 wt.%Na Cl solution revealed 2 orders of magnitude higher that of blank WEP(1.17×10^(7)Ωcm^(2)).With artificial cracks on its coatings,fGO/WEP had no obvious rust compared with blank WEP after 240 h of immersion.We anticipate that self-healing and physical barrier bi-functional nanocontainers improve the traditional anticorrosion coating efficiency with better,longer-lasting performance for shipping,oil drilling or bridge maintenance.