NiCoP_(4)O_(12)/NiCoP nanorod-like arrays with tunable grain boundary density and pores were synthesized by the processes composed of hydrothermal and pyrolysis,in which,the electron structure of Ni and Co atoms chara...NiCoP_(4)O_(12)/NiCoP nanorod-like arrays with tunable grain boundary density and pores were synthesized by the processes composed of hydrothermal and pyrolysis,in which,the electron structure of Ni and Co atoms characterized by X-ray photoelectron spectroscopy was contemporaneous inverse manipulated.The optimized NiCoP_(4)O_(12)/NiCoP arrays have a high specific capacitance of 507.8μAh∙cm^(–2)at 1 mA∙cm^(–2),and good rate ability of 64.7%retention at 30-folds increased current density.Importantly,an ultra-stable ability,88.5%of retention after 10000 cycles,was achieved in an asymmetric cell assembled of the NiCoP_(4)O_(12)/NiCoP arrays with activated carbon.In addition,the energy and power densities of an asymmetric cell were higher than those of other work,demonstrating as-prepared NiCoP_(4)O_(12)/NiCoP arrays are promising electrodes for supercapacitors.展开更多
基金he Natural Science Foundation of Shandong Province of China(Grant No.ZR2020MB024)and the Open Project Program of Guangdong Provincial Key Laboratory for Electronic Functional Materials and Devices,Huizhou University(Grant No.EFMD2021001Z)for financially supporting this work.
文摘NiCoP_(4)O_(12)/NiCoP nanorod-like arrays with tunable grain boundary density and pores were synthesized by the processes composed of hydrothermal and pyrolysis,in which,the electron structure of Ni and Co atoms characterized by X-ray photoelectron spectroscopy was contemporaneous inverse manipulated.The optimized NiCoP_(4)O_(12)/NiCoP arrays have a high specific capacitance of 507.8μAh∙cm^(–2)at 1 mA∙cm^(–2),and good rate ability of 64.7%retention at 30-folds increased current density.Importantly,an ultra-stable ability,88.5%of retention after 10000 cycles,was achieved in an asymmetric cell assembled of the NiCoP_(4)O_(12)/NiCoP arrays with activated carbon.In addition,the energy and power densities of an asymmetric cell were higher than those of other work,demonstrating as-prepared NiCoP_(4)O_(12)/NiCoP arrays are promising electrodes for supercapacitors.