Corrosion behavior of 2024 Al-Cu-Mg alloy of different tempers was assessed by potentiodynamic polarization studies in 3.5% NaCl solution, 3.5% NaCI＋I.0% H2O2 solution and 3.5% NaCl solution at pH 12. Polarization cu...Corrosion behavior of 2024 Al-Cu-Mg alloy of different tempers was assessed by potentiodynamic polarization studies in 3.5% NaCl solution, 3.5% NaCI＋I.0% H2O2 solution and 3.5% NaCl solution at pH 12. Polarization curves showed shifting of corrosion potential （φPcor） towards more negative potential with increasing ageing time and shifting of φcorr in the positive direction with the addition of H2O2 in NaCl solution. Polarization curves in 3.5% NaCl solution at pH 12 exhibited distinct passivity phenomenon. Optical micrographs of the corroded surfaces showed general corrosion, extensive pitting and intergranular corrosion as well. Cyclic potentiodynamic polarization curves exhibited wide hysteresis loop and the mode of corrosion attack confirmed that the alloy states are susceptible to pit growth damage. Attempts were made to explain the observed corrosion behavior of the alloy of various tempers in different electrolytes with the help of microstructural features.展开更多
文摘Corrosion behavior of 2024 Al-Cu-Mg alloy of different tempers was assessed by potentiodynamic polarization studies in 3.5% NaCl solution, 3.5% NaCI＋I.0% H2O2 solution and 3.5% NaCl solution at pH 12. Polarization curves showed shifting of corrosion potential （φPcor） towards more negative potential with increasing ageing time and shifting of φcorr in the positive direction with the addition of H2O2 in NaCl solution. Polarization curves in 3.5% NaCl solution at pH 12 exhibited distinct passivity phenomenon. Optical micrographs of the corroded surfaces showed general corrosion, extensive pitting and intergranular corrosion as well. Cyclic potentiodynamic polarization curves exhibited wide hysteresis loop and the mode of corrosion attack confirmed that the alloy states are susceptible to pit growth damage. Attempts were made to explain the observed corrosion behavior of the alloy of various tempers in different electrolytes with the help of microstructural features.