To address the issues of short setting time and high bleeding rate of A component,which easily cause pipe plugging and poor grouting performance when a two-component grout is injected synchronously behind the Segmenta...To address the issues of short setting time and high bleeding rate of A component,which easily cause pipe plugging and poor grouting performance when a two-component grout is injected synchronously behind the Segmental Lining,the inorganic retarder sodium pyrophosphate(TSPP)and three organic retarders were added to the A component:sodium citrate(SC),sodium tartrate(ST)and glycerol(GLY).The effect law and microscopic mechanism of viscosity,bleeding rate,setting time,gelling time,compressive strength,and stone rate were investigated.The results revealed that the addition of retarders could enhance the stability and setting time of the A component and increase the gelling time,stone rate,and compressive strength of two-component grout.Among them,the performance of the grout with an SC dosage of 0.1% was superior.The bleeding rate of this grout was reduced to 3.5%,the stone rate of the two-component grout was more than 99%,and the early compressive strength and late compressive strength of this grout were increased by approximately 35% and 7%,respectively.The initial and final setting time of the A component with a TSPP dosage of 0.3% was the longest,which was prolonged to 17 and 26 h,respectively.Microscopic analysis revealed that the four retarders hindered the hydration process of cement through complexation and adsorption,and inhibited the hydration of C_(3)S and the crystallisation of CH.Moreover,they reduced the defects caused by the rapid reaction of water glass and CH on the solid phase structure,enabled the microstructure of the stone body to be denser,and subsequently,enhanced the compressive strength.展开更多
The effects of ultrafine WC(WC_(UF),0.5μm) or W(1μm) and C(0.3μm)(W+C)_(UF) additives on the densification,microstructure and mechanical properties of coarse-grained cemented carbides were compared systematically.O...The effects of ultrafine WC(WC_(UF),0.5μm) or W(1μm) and C(0.3μm)(W+C)_(UF) additives on the densification,microstructure and mechanical properties of coarse-grained cemented carbides were compared systematically.Overall,the cemented carbides with WC_(UF)/(W+C)_(UF) additives are almost fully densification to be higher than 99%,and the average grain size is kept above 2.8μm.The WC_(UF) additive assists grains to(truncated)trigonal prism shape by two dimensional(2D) growth,whereas the(W+C)_(UF) additive assists grains to rounded shape by three dimensional(3D) growth,lowers WC contiguity and increases face-centered-cubic Co.The hardness and bending strength of(75WC_(C)-15WC_(UF))-10Co are 86.6 HRA and 2 272 MPa,respectively,both higher than those of(75WC_(C)-15(W+C)_(UF))-10Co,which could be ascribed to the enhanced densification and unblemished grains.However,the fracture toughness of the(75WC_(C)-15(W+C)_(UF))-10Co is 23.5 MPa·m^(1/2),higher than that of the(75WC_(C)-15WC_(UF))-10Co due to the uniform WC-Co structure and flexible binder phase.展开更多
Ni nanoparticles were coated uniformly on the surface of WC powder via a facile electroless plating method(abbreviated as WCN-EP),and then consolidated for mechanical and corrosion resistance performance characterizat...Ni nanoparticles were coated uniformly on the surface of WC powder via a facile electroless plating method(abbreviated as WCN-EP),and then consolidated for mechanical and corrosion resistance performance characterization,in comparison with hand mixed WC-Ni(WCN-H).Under the optimized electroless plating parameters,Ni particles,less than 1μm in average diameter,were found to be uniformly and densely wrapped on the surface of the tungsten carbide matrix of WCN-EP.In comparison,in WCN-H,the Ni particles about 1.8μm in average diameter,were randomly distributed together with irregular WC particles.The uniform coating of Ni was found to assist the densification process of WCN-EP effectively,with higher densities and less pores than those of WCN-H at the Ni content of 10.6wt%,25.5wt%,and 30.3 wt%.However,at the Ni content of 18.8wt%,the relative densities of WCN-EP and WCN-H both increased to the maximum value of 98%.The maximum hardness of the consolidated WCN-EP was 82.6 HRA,about 1.2 HRA higher than that of WCN-H.In addition,the consolidated WCN-EP also exhibits a superior corrosion resistance by the polarization curve analysis at an electrochemical workstation.展开更多
基金Funded by the National Natural Science Foundation of China(No.52378394)the Fundamental Research Funds for the Central Universities(No.B230201037)。
文摘To address the issues of short setting time and high bleeding rate of A component,which easily cause pipe plugging and poor grouting performance when a two-component grout is injected synchronously behind the Segmental Lining,the inorganic retarder sodium pyrophosphate(TSPP)and three organic retarders were added to the A component:sodium citrate(SC),sodium tartrate(ST)and glycerol(GLY).The effect law and microscopic mechanism of viscosity,bleeding rate,setting time,gelling time,compressive strength,and stone rate were investigated.The results revealed that the addition of retarders could enhance the stability and setting time of the A component and increase the gelling time,stone rate,and compressive strength of two-component grout.Among them,the performance of the grout with an SC dosage of 0.1% was superior.The bleeding rate of this grout was reduced to 3.5%,the stone rate of the two-component grout was more than 99%,and the early compressive strength and late compressive strength of this grout were increased by approximately 35% and 7%,respectively.The initial and final setting time of the A component with a TSPP dosage of 0.3% was the longest,which was prolonged to 17 and 26 h,respectively.Microscopic analysis revealed that the four retarders hindered the hydration process of cement through complexation and adsorption,and inhibited the hydration of C_(3)S and the crystallisation of CH.Moreover,they reduced the defects caused by the rapid reaction of water glass and CH on the solid phase structure,enabled the microstructure of the stone body to be denser,and subsequently,enhanced the compressive strength.
基金Funded by the Technology Innovation Leading Program of Shaanxi(No.2022QFY08-02)。
文摘The effects of ultrafine WC(WC_(UF),0.5μm) or W(1μm) and C(0.3μm)(W+C)_(UF) additives on the densification,microstructure and mechanical properties of coarse-grained cemented carbides were compared systematically.Overall,the cemented carbides with WC_(UF)/(W+C)_(UF) additives are almost fully densification to be higher than 99%,and the average grain size is kept above 2.8μm.The WC_(UF) additive assists grains to(truncated)trigonal prism shape by two dimensional(2D) growth,whereas the(W+C)_(UF) additive assists grains to rounded shape by three dimensional(3D) growth,lowers WC contiguity and increases face-centered-cubic Co.The hardness and bending strength of(75WC_(C)-15WC_(UF))-10Co are 86.6 HRA and 2 272 MPa,respectively,both higher than those of(75WC_(C)-15(W+C)_(UF))-10Co,which could be ascribed to the enhanced densification and unblemished grains.However,the fracture toughness of the(75WC_(C)-15(W+C)_(UF))-10Co is 23.5 MPa·m^(1/2),higher than that of the(75WC_(C)-15WC_(UF))-10Co due to the uniform WC-Co structure and flexible binder phase.
基金Funded by the National Natural Science Foundation of China(Nos.51778213 and 52078189)the Fundamental Research Funds for the Central Universities of China(No.B200202073)。
文摘Ni nanoparticles were coated uniformly on the surface of WC powder via a facile electroless plating method(abbreviated as WCN-EP),and then consolidated for mechanical and corrosion resistance performance characterization,in comparison with hand mixed WC-Ni(WCN-H).Under the optimized electroless plating parameters,Ni particles,less than 1μm in average diameter,were found to be uniformly and densely wrapped on the surface of the tungsten carbide matrix of WCN-EP.In comparison,in WCN-H,the Ni particles about 1.8μm in average diameter,were randomly distributed together with irregular WC particles.The uniform coating of Ni was found to assist the densification process of WCN-EP effectively,with higher densities and less pores than those of WCN-H at the Ni content of 10.6wt%,25.5wt%,and 30.3 wt%.However,at the Ni content of 18.8wt%,the relative densities of WCN-EP and WCN-H both increased to the maximum value of 98%.The maximum hardness of the consolidated WCN-EP was 82.6 HRA,about 1.2 HRA higher than that of WCN-H.In addition,the consolidated WCN-EP also exhibits a superior corrosion resistance by the polarization curve analysis at an electrochemical workstation.