One-dimensional titanium dioxide(TiO_(2))whiskers with controllable aspect ratios were synthesized by molten salt method adopting anatase TiO_(2)nanoparticles as precursor,sodium chloride(NaCl)and dibasic sodium phosp...One-dimensional titanium dioxide(TiO_(2))whiskers with controllable aspect ratios were synthesized by molten salt method adopting anatase TiO_(2)nanoparticles as precursor,sodium chloride(NaCl)and dibasic sodium phosphate(Na_(2)HPO_(4))as medium.The particle size of TiO_(2)nanoparticles and ratio of precursor and medium that can help to generate high aspect ratio TiO_(2)whiskers were studied and selected.Light-colored antimony-doped tin oxide@titanium dioxide(ATO@TiO_(2))conductive whiskers were prepared by coating ATO on TiO_(2)whiskers through coprecipitation then.Finally,the ATO@TiO_(2)light-colored conductive whiskers were dispersed in polyacrylonitrile(PAN)to fabricate light-colored conductive fibers.The experimental results show that the ATO@TiO_(2)whiskers exhibits ideal whiteness and conductivity with 65.5 Wb and 106Ω·cm,respectively,and the resistivity of conductive fibers was 6.07×10^(6)Ω·cm with 15wt%whisker content.展开更多
基金Funded by the National Natural Science Foundation of China(No.51803076)the Natural Science Foundation of Jiangsu Province of China(No.BK20180629)+1 种基金the China Postdoctoral Science Foundation(No.2018M632231)the Key Laboratory of Special Protective Textiles of Ministry of Education(Jiangnan University)(No.TZFH-24-006)。
文摘One-dimensional titanium dioxide(TiO_(2))whiskers with controllable aspect ratios were synthesized by molten salt method adopting anatase TiO_(2)nanoparticles as precursor,sodium chloride(NaCl)and dibasic sodium phosphate(Na_(2)HPO_(4))as medium.The particle size of TiO_(2)nanoparticles and ratio of precursor and medium that can help to generate high aspect ratio TiO_(2)whiskers were studied and selected.Light-colored antimony-doped tin oxide@titanium dioxide(ATO@TiO_(2))conductive whiskers were prepared by coating ATO on TiO_(2)whiskers through coprecipitation then.Finally,the ATO@TiO_(2)light-colored conductive whiskers were dispersed in polyacrylonitrile(PAN)to fabricate light-colored conductive fibers.The experimental results show that the ATO@TiO_(2)whiskers exhibits ideal whiteness and conductivity with 65.5 Wb and 106Ω·cm,respectively,and the resistivity of conductive fibers was 6.07×10^(6)Ω·cm with 15wt%whisker content.