0.5AFeO_(3)-0.5NaNbO_(3)(A=Bi,La)solid solution compositions were prepared using a solid phase reaction route from high-purity starting oxides.Mossbauer studies have shown that while for 0.5BiFeO_(3)-0.5NaNbO_(3)the m...0.5AFeO_(3)-0.5NaNbO_(3)(A=Bi,La)solid solution compositions were prepared using a solid phase reaction route from high-purity starting oxides.Mossbauer studies have shown that while for 0.5BiFeO_(3)-0.5NaNbO_(3)the magnetic phase transition temperature T_(M) value is about 150 K,for 0.5LaFeO_(3)-0.5NaNbO_(3),it is only≈25 K.This dramatic difference in T_(M) values seems to be due to additional contribution of the magnetic superexchange between Fe^(3+)ions via the empty 6p-states of Bi^(3+)ions to the overall superexchange.展开更多
基金This work was supported by RFBR and NSFC,project 19-52-53030 GFEN a and by the Ministry of Education and Science of the Russian Federation(State assignment in the field of scientific activity,Southern Federal University,2020).
文摘0.5AFeO_(3)-0.5NaNbO_(3)(A=Bi,La)solid solution compositions were prepared using a solid phase reaction route from high-purity starting oxides.Mossbauer studies have shown that while for 0.5BiFeO_(3)-0.5NaNbO_(3)the magnetic phase transition temperature T_(M) value is about 150 K,for 0.5LaFeO_(3)-0.5NaNbO_(3),it is only≈25 K.This dramatic difference in T_(M) values seems to be due to additional contribution of the magnetic superexchange between Fe^(3+)ions via the empty 6p-states of Bi^(3+)ions to the overall superexchange.