The repair welding of UNS C95700manganese?aluminum bronze plates was done using different filler metals.Themicrostructure and mechanical properties of welds were studied.The main microstructural constituents wereα,β...The repair welding of UNS C95700manganese?aluminum bronze plates was done using different filler metals.Themicrostructure and mechanical properties of welds were studied.The main microstructural constituents wereα,βandκphases withdifferent morphologies.The addition of manganese decreased the percentage ofαphase in the microstructure of weldments from80%(Mn-free weld)to57%(12.5%Mn weld,mass fraction).The morphology ofκphase was lamellar in high nickel specimens andit was changed to a globular morphology for high manganese welds.Although the application of high manganese filler metal yieldedthe higher tensile and bending strengths of weldment compared with the weld using high nickel filler material,the optimummechanical properties of repair welds were obtained using a non-alloy filler material(ERCuAl-A2)for the underlay and highmanganese filler metal(ERCuMnNiAl)for filling passes.This weld presented an increase of39%in tensile strength compared withthe base metal,and no cracking was observed after bending test.展开更多
文摘The repair welding of UNS C95700manganese?aluminum bronze plates was done using different filler metals.Themicrostructure and mechanical properties of welds were studied.The main microstructural constituents wereα,βandκphases withdifferent morphologies.The addition of manganese decreased the percentage ofαphase in the microstructure of weldments from80%(Mn-free weld)to57%(12.5%Mn weld,mass fraction).The morphology ofκphase was lamellar in high nickel specimens andit was changed to a globular morphology for high manganese welds.Although the application of high manganese filler metal yieldedthe higher tensile and bending strengths of weldment compared with the weld using high nickel filler material,the optimummechanical properties of repair welds were obtained using a non-alloy filler material(ERCuAl-A2)for the underlay and highmanganese filler metal(ERCuMnNiAl)for filling passes.This weld presented an increase of39%in tensile strength compared withthe base metal,and no cracking was observed after bending test.