The nanocrystalline samples Nd_(1-x)M_(x)FeO_(3)(x=0.0 and 0.1;M:Co^(2+)and Ni^(2+))were prepared using the citrate combustion method.The X-ray diffraction(XRD)pattern confirmed that the nanoparticles were synthesized...The nanocrystalline samples Nd_(1-x)M_(x)FeO_(3)(x=0.0 and 0.1;M:Co^(2+)and Ni^(2+))were prepared using the citrate combustion method.The X-ray diffraction(XRD)pattern confirmed that the nanoparticles were synthesized in an orthorhombic structure.The particle size of Nd_(1-x)M_(x)FeO_(3) is in the range of 29-59 nm.The selected area electron diffraction(SAED)indicates the samples were prepared in a polycrystalline nature.The samples Nd_(1-x)M_(x)FeO_(3)(x=0.0 and 0.1;M:Co^(2+)and Ni^(2+))have anti ferromagnetic behavior.The Fe^(3+)spins are aligned antiparallel,forming the antiferromagnetic(AFM)properties,which are affected by many factors such as the bond angle between the Fe^(3+)(Fe^(3+)-O_(2)--Fe^(3+))and the Dzyaloshinskii-Moriya(D-M)interaction.The doping of Co^(2+)and Ni^(2+)ions in NdFeO_(3) enhances the magnetic properties of the NdFeO_(3).The saturation magnetization(Ms)of Nd_(0.90)Co_(0.10)FeO_(3) increases 1.8times more than that of NdFeO_(3).The exchange bias field(HEX)of the Co-doped sample is two times greater than that of NdFeO_(3).The magnetic anisotropy constant(K)of the 10%Co-doped sample increases by 11 factors compared to that of NdFeO_(3).The Tauc plot illustrates that the samples have a direct optical transition.The divalent cation substitution(Co^(2+)and Ni^(2+))decreases the optical band gap of NdFeO_(3),leading to the recommendation of using the samples Nd_(0.90)Co_(0.10)FeO_(3) and Nd_(0.90)Ni_(0.10)FeO_(3) in photocatalysis of dye degradation from water.The removal efficiencies of Cr6+at pH=6 are 88.06%,85.54%,and 85.52%for the samples NdFeO_(3),Nd_(0.90)Co_(0.10)FeO_(3),and Nd_(0.90)Ni_(0.10)FeO_(3),respectively.The Freundlich isotherm mode is the best-fit model for NdFeO_(3) to adsorb Cr6+ions from aqueous solutions.展开更多
文摘The nanocrystalline samples Nd_(1-x)M_(x)FeO_(3)(x=0.0 and 0.1;M:Co^(2+)and Ni^(2+))were prepared using the citrate combustion method.The X-ray diffraction(XRD)pattern confirmed that the nanoparticles were synthesized in an orthorhombic structure.The particle size of Nd_(1-x)M_(x)FeO_(3) is in the range of 29-59 nm.The selected area electron diffraction(SAED)indicates the samples were prepared in a polycrystalline nature.The samples Nd_(1-x)M_(x)FeO_(3)(x=0.0 and 0.1;M:Co^(2+)and Ni^(2+))have anti ferromagnetic behavior.The Fe^(3+)spins are aligned antiparallel,forming the antiferromagnetic(AFM)properties,which are affected by many factors such as the bond angle between the Fe^(3+)(Fe^(3+)-O_(2)--Fe^(3+))and the Dzyaloshinskii-Moriya(D-M)interaction.The doping of Co^(2+)and Ni^(2+)ions in NdFeO_(3) enhances the magnetic properties of the NdFeO_(3).The saturation magnetization(Ms)of Nd_(0.90)Co_(0.10)FeO_(3) increases 1.8times more than that of NdFeO_(3).The exchange bias field(HEX)of the Co-doped sample is two times greater than that of NdFeO_(3).The magnetic anisotropy constant(K)of the 10%Co-doped sample increases by 11 factors compared to that of NdFeO_(3).The Tauc plot illustrates that the samples have a direct optical transition.The divalent cation substitution(Co^(2+)and Ni^(2+))decreases the optical band gap of NdFeO_(3),leading to the recommendation of using the samples Nd_(0.90)Co_(0.10)FeO_(3) and Nd_(0.90)Ni_(0.10)FeO_(3) in photocatalysis of dye degradation from water.The removal efficiencies of Cr6+at pH=6 are 88.06%,85.54%,and 85.52%for the samples NdFeO_(3),Nd_(0.90)Co_(0.10)FeO_(3),and Nd_(0.90)Ni_(0.10)FeO_(3),respectively.The Freundlich isotherm mode is the best-fit model for NdFeO_(3) to adsorb Cr6+ions from aqueous solutions.
