In this study,an experimental analysis for determining the fatigue strength of HDPE-100 under cyclic loading is presented.The curve of cumulative fatigue damage versus number of cycles(D-N)was deduced from stiffness d...In this study,an experimental analysis for determining the fatigue strength of HDPE-100 under cyclic loading is presented.The curve of cumulative fatigue damage versus number of cycles(D-N)was deduced from stiffness degradation.Based on the three stage damage trend,the remaining fatigue life is numerically predicted by considering a double term power damage accumulation model.This model is found to be accurate,both in modeling the rapid damage growth in the early life and near the end of the fatigue life.Numerical results illustrate that the proposed model is capable of accurately fitting several different sets of experimental data.展开更多
Impact behavior of polymers has received considerable attention in recent years,and much work based on fracture mechanic approaches has been carried out.In this paper,fracture behavior in large deformation of a high d...Impact behavior of polymers has received considerable attention in recent years,and much work based on fracture mechanic approaches has been carried out.In this paper,fracture behavior in large deformation of a high density polyethylene(HDPE)materials was investigated through experimental impact testing on single edge notched specimen(SENB)and by using theoretical and analytical fracture criteria concepts.Moreover,a review of the main fracture criteria is given in order to characterize the toughness of this polymer in the both cases(static and dynamic).The fractured specimens obtained from the Charpy impact test were characterized with respect to their fracture surfaces.Characteristic zones of the fracture surface can be assigned to different stages and mechanisms of the fracture process.Finally,for a better understanding of fracture and damage mechanisms and to provide the best estimation of fracture toughness in impact,an experimental approach based on microscopic observations(SEM)was used.展开更多
文摘In this study,an experimental analysis for determining the fatigue strength of HDPE-100 under cyclic loading is presented.The curve of cumulative fatigue damage versus number of cycles(D-N)was deduced from stiffness degradation.Based on the three stage damage trend,the remaining fatigue life is numerically predicted by considering a double term power damage accumulation model.This model is found to be accurate,both in modeling the rapid damage growth in the early life and near the end of the fatigue life.Numerical results illustrate that the proposed model is capable of accurately fitting several different sets of experimental data.
文摘Impact behavior of polymers has received considerable attention in recent years,and much work based on fracture mechanic approaches has been carried out.In this paper,fracture behavior in large deformation of a high density polyethylene(HDPE)materials was investigated through experimental impact testing on single edge notched specimen(SENB)and by using theoretical and analytical fracture criteria concepts.Moreover,a review of the main fracture criteria is given in order to characterize the toughness of this polymer in the both cases(static and dynamic).The fractured specimens obtained from the Charpy impact test were characterized with respect to their fracture surfaces.Characteristic zones of the fracture surface can be assigned to different stages and mechanisms of the fracture process.Finally,for a better understanding of fracture and damage mechanisms and to provide the best estimation of fracture toughness in impact,an experimental approach based on microscopic observations(SEM)was used.
