The microstructure and impact behavior of A356 aluminum alloy were studied after melt treatment processes of grain refinement and modification under both non-heat treated and T6 heat treated conditions. The modificati...The microstructure and impact behavior of A356 aluminum alloy were studied after melt treatment processes of grain refinement and modification under both non-heat treated and T6 heat treated conditions. The modification and grain refinement were done with the addition of Al-10%Sr and Al-5Ti-1B master alloys, respectively. All casting parameters were kept constant in order to focus on the influence of mentioned treatments. The results indicate that the eutectic silicon morphology is the main parameter to control the impact behavior of alloy. Consequently, the individual grain refinement of as-cast alloy does not improve the impact toughness as the modification does. While, simultaneous grain refinement and modification provide higher impact toughness in comparison with individual treatments. T6 heat treatment of the alloy improves the impact toughness under all melt-treated conditions. This is related to the further modification of eutectic silicon particles. To verify the results and clarify the mechanisms, three-point bending test and fractography were used to interpret the improvement of impact toughness of the alloy.展开更多
文摘The microstructure and impact behavior of A356 aluminum alloy were studied after melt treatment processes of grain refinement and modification under both non-heat treated and T6 heat treated conditions. The modification and grain refinement were done with the addition of Al-10%Sr and Al-5Ti-1B master alloys, respectively. All casting parameters were kept constant in order to focus on the influence of mentioned treatments. The results indicate that the eutectic silicon morphology is the main parameter to control the impact behavior of alloy. Consequently, the individual grain refinement of as-cast alloy does not improve the impact toughness as the modification does. While, simultaneous grain refinement and modification provide higher impact toughness in comparison with individual treatments. T6 heat treatment of the alloy improves the impact toughness under all melt-treated conditions. This is related to the further modification of eutectic silicon particles. To verify the results and clarify the mechanisms, three-point bending test and fractography were used to interpret the improvement of impact toughness of the alloy.