High-entropy materials have become high-activity electrocatalysis owing to their high-entropy effect and multiple active sites.Herein,we synthesize a series of carbon-supported nano high-entropy oxides(HEOs/C),specifi...High-entropy materials have become high-activity electrocatalysis owing to their high-entropy effect and multiple active sites.Herein,we synthesize a series of carbon-supported nano high-entropy oxides(HEOs/C),specifically (PtFeCoNiCu)O/C,using a carbothermal shock (CTS) method for application as a cathode catalyst in direct borohydride fuel cells (DBFCs).The microstructure of the prepared catalysts was characterized by X-ray photoelectron spectroscopy,X-ray absorption fine structure,and transmission electron microscopy.The prepared (PtFeCoNiCu)O/C,with particle sizes ranging from 2 to 4 nm,demonstrates 3.94 transferred electrons towards the oxygen reduction reaction in an alkaline environment,resulting in a minimal H_(2)O_(2)yield of 2.6%.Additionally,it exhibits a Tafel slope of 61 mV dec-1,surpassing that of commercial Pt/C (82 mV dec-1).Furthermore,after 40,000 cycles of cyclic voltammetry(CV) testing,the half-wave potential of (PtFeCoNiCu)O/C shows a positive shift of 3 mV,with no notable decline in the limiting current density.When (PtFeCoNiCu)O/C is used as a cathode catalyst in DBFCs,the DBFC achieves a maximum power density of 441 mW cm^(-2)at 60°C and sustains a cell voltage of approximately 0.73 V after 52 h at 30°C.These findings confirm that HEO/C is a promising cathode catalyst for DBFCs.展开更多
基金Zhejiang Provincial Natural Science Foundation of China (LZ22B060001,LY22E010003)“Pioneer” R&D Program of Zhejiang Province(2023C01080)National Natural Science Foundation of China (52301235)。
文摘High-entropy materials have become high-activity electrocatalysis owing to their high-entropy effect and multiple active sites.Herein,we synthesize a series of carbon-supported nano high-entropy oxides(HEOs/C),specifically (PtFeCoNiCu)O/C,using a carbothermal shock (CTS) method for application as a cathode catalyst in direct borohydride fuel cells (DBFCs).The microstructure of the prepared catalysts was characterized by X-ray photoelectron spectroscopy,X-ray absorption fine structure,and transmission electron microscopy.The prepared (PtFeCoNiCu)O/C,with particle sizes ranging from 2 to 4 nm,demonstrates 3.94 transferred electrons towards the oxygen reduction reaction in an alkaline environment,resulting in a minimal H_(2)O_(2)yield of 2.6%.Additionally,it exhibits a Tafel slope of 61 mV dec-1,surpassing that of commercial Pt/C (82 mV dec-1).Furthermore,after 40,000 cycles of cyclic voltammetry(CV) testing,the half-wave potential of (PtFeCoNiCu)O/C shows a positive shift of 3 mV,with no notable decline in the limiting current density.When (PtFeCoNiCu)O/C is used as a cathode catalyst in DBFCs,the DBFC achieves a maximum power density of 441 mW cm^(-2)at 60°C and sustains a cell voltage of approximately 0.73 V after 52 h at 30°C.These findings confirm that HEO/C is a promising cathode catalyst for DBFCs.