The synthesis and luminescence properties of Zn2 SiO4: Mn phosphor layers on spherical silica spheres, i.e.,a kind of core-shell complex phosphor, Zn2SiO4: Mn@ SiO2 were described.Firstly, monodisperse silica spheres ...The synthesis and luminescence properties of Zn2 SiO4: Mn phosphor layers on spherical silica spheres, i.e.,a kind of core-shell complex phosphor, Zn2SiO4: Mn@ SiO2 were described.Firstly, monodisperse silica spheres were obtained via the Stober method by the hydrolysis of tetraethoxysilane(TEOS) Si ( OC2H5 ) 4 under base condition ( using NH4 OH as the catalyst).Secondly, the silica spheres were coated with a Zn2 SiO4: Mn phosphor layer by a Pechini solgel process.X-ray diffraction ( XRD), scanning electron microscope ( SEM), energy-dispersive X-ray spectrum ( EDS )and photoluminescence (PL) were employed to characterize the resulting complex phosphor.The results confirm that1000 ℃ annealed sample consists of crystalline Zn2SiO4: Mn shells and amorphous SiO2 cores.The phosphor show the green emission of Mn2+ at 521 nm corresponding 4T1 (4G) - 6 A1 (6S) transition, and the possible luminescence mechanism is proposed.展开更多
文摘The synthesis and luminescence properties of Zn2 SiO4: Mn phosphor layers on spherical silica spheres, i.e.,a kind of core-shell complex phosphor, Zn2SiO4: Mn@ SiO2 were described.Firstly, monodisperse silica spheres were obtained via the Stober method by the hydrolysis of tetraethoxysilane(TEOS) Si ( OC2H5 ) 4 under base condition ( using NH4 OH as the catalyst).Secondly, the silica spheres were coated with a Zn2 SiO4: Mn phosphor layer by a Pechini solgel process.X-ray diffraction ( XRD), scanning electron microscope ( SEM), energy-dispersive X-ray spectrum ( EDS )and photoluminescence (PL) were employed to characterize the resulting complex phosphor.The results confirm that1000 ℃ annealed sample consists of crystalline Zn2SiO4: Mn shells and amorphous SiO2 cores.The phosphor show the green emission of Mn2+ at 521 nm corresponding 4T1 (4G) - 6 A1 (6S) transition, and the possible luminescence mechanism is proposed.