The bonding of a steel plate to Al-20Sn slurry was conducted using thecasting rolling technique. The surface of the steel plate was defatted, descaled, immersed (inK_2ZrF_6 flux aqueous solution) and stoved. Al-20Sn s...The bonding of a steel plate to Al-20Sn slurry was conducted using thecasting rolling technique. The surface of the steel plate was defatted, descaled, immersed (inK_2ZrF_6 flux aqueous solution) and stoved. Al-20Sn slurry was prepared using the electromagneticmechanical starring method. The interfacial mechanical property of the bonding plate was researchedto determine the relationship between the diffusion time and the interfacial shear strength. Inorder to identify the mechanism of bonding, the interfacial structure of the bonding plate wasstudied. The results show that at a prebeat temperature of the steel plate of 505 deg C and a solidfraction of Al-20Sn slurry of 35 percent, the relationship between the interfacial shear strength Sand the diffusion time t is S=28.8+4.3t-0.134t^2 +0.0011t^3. When the diffusion time is 22 s, thelargest interfacial shear strength is 70.3 MPa, and the corresponding interface is a new one whichis made up of Fe-Al compound and Fe-Al solid solution alternatively and in a right proportion. Inthis interfacial structure, the interfacial embrittlement does not happen and Fe-Al compound canplay its role in strong combination adequately.展开更多
基金This work was supported by the National Natural Science Foundation of China (No.50274047)Beijing Jiaotong University Foundation
文摘The bonding of a steel plate to Al-20Sn slurry was conducted using thecasting rolling technique. The surface of the steel plate was defatted, descaled, immersed (inK_2ZrF_6 flux aqueous solution) and stoved. Al-20Sn slurry was prepared using the electromagneticmechanical starring method. The interfacial mechanical property of the bonding plate was researchedto determine the relationship between the diffusion time and the interfacial shear strength. Inorder to identify the mechanism of bonding, the interfacial structure of the bonding plate wasstudied. The results show that at a prebeat temperature of the steel plate of 505 deg C and a solidfraction of Al-20Sn slurry of 35 percent, the relationship between the interfacial shear strength Sand the diffusion time t is S=28.8+4.3t-0.134t^2 +0.0011t^3. When the diffusion time is 22 s, thelargest interfacial shear strength is 70.3 MPa, and the corresponding interface is a new one whichis made up of Fe-Al compound and Fe-Al solid solution alternatively and in a right proportion. Inthis interfacial structure, the interfacial embrittlement does not happen and Fe-Al compound canplay its role in strong combination adequately.