The microstructure, texture characteristics and torsion ability of two kinds of steel wires were investigated. The eutectoid steel wires were produced by hot and cold drawing with severe deformation. The torsinability...The microstructure, texture characteristics and torsion ability of two kinds of steel wires were investigated. The eutectoid steel wires were produced by hot and cold drawing with severe deformation. The torsinability of steel wires was measured under two cases, i.e. there exists either fiber texture or circular texture. The results showed that the torsional behavior of the steel wires was affected by their textures and microstructures. The {110}<110> circular texture weakened the torsion ability of the wires. The torsion fracture behavior of {110}<110> texture wires is related to the fact that only two slip systems were activated under simple shear strain deformation.展开更多
The texture inhomogeneity in cross shear rolled grain oriented Si steel was investigated by means of the through thickness texture analysis. For the chosen rolling reductions (55%, 66.5%) and mismatch speed ratios (1....The texture inhomogeneity in cross shear rolled grain oriented Si steel was investigated by means of the through thickness texture analysis. For the chosen rolling reductions (55%, 66.5%) and mismatch speed ratios (1.0, 1.1, 1.3), the deformation textures in various thickness layers consist of three major components, i.e. strong γ-fiber, medium α-fiber and weak η-fiber, and they show an asymmetrical distribution throughout the thickness. The effect of reduction on the texture gradient is found to be more significant at and near the center layer; however, the effect of mismatch speed ratio is less important. In most cases, a strong {111}<112> texture component appears in the subsurface layers, that may favour the formation of a sharp Goss texture during the subsequent annealing.展开更多
基金This work is supported by key project of the National Nat-ural Science Foundation of China(Grant No.50231030)the National High Technology Research and Development Pro-gram of China(Grant No.2003AA331030)the Teaching and Research Award Program for Outstanding Young Teach-ers in Higher Education Institutions.
文摘The microstructure, texture characteristics and torsion ability of two kinds of steel wires were investigated. The eutectoid steel wires were produced by hot and cold drawing with severe deformation. The torsinability of steel wires was measured under two cases, i.e. there exists either fiber texture or circular texture. The results showed that the torsional behavior of the steel wires was affected by their textures and microstructures. The {110}<110> circular texture weakened the torsion ability of the wires. The torsion fracture behavior of {110}<110> texture wires is related to the fact that only two slip systems were activated under simple shear strain deformation.
基金This work was supported by the National Natural Science Foundation of China (No. 59671037 and 50071061).
文摘The texture inhomogeneity in cross shear rolled grain oriented Si steel was investigated by means of the through thickness texture analysis. For the chosen rolling reductions (55%, 66.5%) and mismatch speed ratios (1.0, 1.1, 1.3), the deformation textures in various thickness layers consist of three major components, i.e. strong γ-fiber, medium α-fiber and weak η-fiber, and they show an asymmetrical distribution throughout the thickness. The effect of reduction on the texture gradient is found to be more significant at and near the center layer; however, the effect of mismatch speed ratio is less important. In most cases, a strong {111}<112> texture component appears in the subsurface layers, that may favour the formation of a sharp Goss texture during the subsequent annealing.