A new pretreatment method has been developed to improve the catalytic activity of the Ni-Fe-Mo-Co alloy electrode for hydrogen evolution reaction （HER）. The procedure involves pre-electrolyzing the Ni-Fe-Mo-Co alloy...A new pretreatment method has been developed to improve the catalytic activity of the Ni-Fe-Mo-Co alloy electrode for hydrogen evolution reaction （HER）. The procedure involves pre-electrolyzing the Ni-Fe-Mo-Co alloy electrode in 30% KOH solution containing 10% potassium sodium tartrate at 70℃ for 2 h, until some of the Mo and Fe elements are leached out. The surface morphology of the Ni-Fe-Mo-Co alloy demonstrates a unique hive-like structure after the pre- treatment, which has the pore size in a nanometer range （about 50 nm）, a very large real surface area, and good stability. The results of the electrochemical studies show that compared to other similar electrode materials and the treated Ni-Fe-Mo-Co electrode by leaching method, the pre-treated Ni-Fe-Mo-Co electrode has a much lower overpotential and much higher exchange current density for HER. In addition, a long-term continuous electrolysis test with a current interruption shows that the Ni-Fe-Mo-Co alloy has excellent catalytic stability.展开更多
文摘A new pretreatment method has been developed to improve the catalytic activity of the Ni-Fe-Mo-Co alloy electrode for hydrogen evolution reaction （HER）. The procedure involves pre-electrolyzing the Ni-Fe-Mo-Co alloy electrode in 30% KOH solution containing 10% potassium sodium tartrate at 70℃ for 2 h, until some of the Mo and Fe elements are leached out. The surface morphology of the Ni-Fe-Mo-Co alloy demonstrates a unique hive-like structure after the pre- treatment, which has the pore size in a nanometer range （about 50 nm）, a very large real surface area, and good stability. The results of the electrochemical studies show that compared to other similar electrode materials and the treated Ni-Fe-Mo-Co electrode by leaching method, the pre-treated Ni-Fe-Mo-Co electrode has a much lower overpotential and much higher exchange current density for HER. In addition, a long-term continuous electrolysis test with a current interruption shows that the Ni-Fe-Mo-Co alloy has excellent catalytic stability.