By introducing the Zener-Hollomon parameter, which synthetically considersthe influence of deformation temperature and strain rate into damage mechanics, a damage evolutionmodel was developed to simulate the damage ev...By introducing the Zener-Hollomon parameter, which synthetically considersthe influence of deformation temperature and strain rate into damage mechanics, a damage evolutionmodel was developed to simulate the damage evolution of metallic materials during hot deformation.The errors between the prediction damage values and the experimental ones are within 6%.展开更多
The tensile deformation hot simulation test of as-cast 1420 Al-Li alloy was performed on Gleeble-1500 Thermal Simulator in the deformation temperature range from 350 to 450 ℃ and the strain rate range from 0.01 to l0...The tensile deformation hot simulation test of as-cast 1420 Al-Li alloy was performed on Gleeble-1500 Thermal Simulator in the deformation temperature range from 350 to 450 ℃ and the strain rate range from 0.01 to l0.0s-1.The tensile fracture behavior of the 1420 Al-Li alloy at high temperature was studied experimently. The results show that the tensile fracture mode of the 1420 Al-Li alloy at high temperature is changed from typical transgranular ductile fracture to intergranular brittle fracture with the increase of the deformation temperature and the strain rate. It is made out that the precipitation of LiH is the fundamental reason for the intergranular brittle fracture of the 1420 Al-Li alloy at high temperature. The mechanism of hydrogen embrittlement of the 1420 Al-Li alloy at high temperature was discussed, and it was proposed that the hydrogen embrittlement at high temperature is an integrated function of the dynamic and the static force, which enrichs the theories of hydrogen embrittlemen t.展开更多
文摘By introducing the Zener-Hollomon parameter, which synthetically considersthe influence of deformation temperature and strain rate into damage mechanics, a damage evolutionmodel was developed to simulate the damage evolution of metallic materials during hot deformation.The errors between the prediction damage values and the experimental ones are within 6%.
文摘The tensile deformation hot simulation test of as-cast 1420 Al-Li alloy was performed on Gleeble-1500 Thermal Simulator in the deformation temperature range from 350 to 450 ℃ and the strain rate range from 0.01 to l0.0s-1.The tensile fracture behavior of the 1420 Al-Li alloy at high temperature was studied experimently. The results show that the tensile fracture mode of the 1420 Al-Li alloy at high temperature is changed from typical transgranular ductile fracture to intergranular brittle fracture with the increase of the deformation temperature and the strain rate. It is made out that the precipitation of LiH is the fundamental reason for the intergranular brittle fracture of the 1420 Al-Li alloy at high temperature. The mechanism of hydrogen embrittlement of the 1420 Al-Li alloy at high temperature was discussed, and it was proposed that the hydrogen embrittlement at high temperature is an integrated function of the dynamic and the static force, which enrichs the theories of hydrogen embrittlemen t.