In this paper,the Ni/Al_(2)O_(3) monolithic catalyst with 15%Ni content was prepared using cordierite as a matrix,and the catalyst was modified with 10%NaOH to study the methanation performance of biomass gasification...In this paper,the Ni/Al_(2)O_(3) monolithic catalyst with 15%Ni content was prepared using cordierite as a matrix,and the catalyst was modified with 10%NaOH to study the methanation performance of biomass gasification simulated gas based on alkali-modified Ni/Al_(2)O_(3) monolithic catalyst.BET,TEM,H_(2)-TPR,XRD,CO_(2)-TPD and TG were used to characterize the physicochemical properties of the catalyst before and after modification.The results indicated that the CO conversion rate trends of unmodified and modified Ni/Al_(2)O_(3) monolithic catalysts over 2 h were fundamentally consistent.However,the Ni/Al_(2)O_(3) catalysts modified for 2 h demonstrated significantly enhanced performance compared to those modified for 1 h.Regarding CH4 selectivity,the modified Ni/Al_(2)O_(3) catalyst exhibited markedly better performance than the unmodified Ni/Al_(2)O_(3) catalyst,confirming the enhanced methane performance of the alkali-modified Ni/Al_(2)O_(3) monolithic catalyst.Under optimized conditions(H_(2)/CO volume ratio of 3∶1,space velocity of 10000 mL/(g·h),and temperature of 400℃),the methanation performance of the Ni/Al_(2)O_(3) monolithic catalyst modified for 2 h reached its peak,achieving a CO conversion rate of 97%with 100%CH4 selectivity.展开更多
基金Supported by the National Natural Science Foundation of China(52506188,52476215)Natural Science Foundation of Liaoning Province(2024-MS-139,2024JH3/10200047)Scientific Research Program of Department of Education of Liaoning Province(310125042,LJ212410143033。
文摘In this paper,the Ni/Al_(2)O_(3) monolithic catalyst with 15%Ni content was prepared using cordierite as a matrix,and the catalyst was modified with 10%NaOH to study the methanation performance of biomass gasification simulated gas based on alkali-modified Ni/Al_(2)O_(3) monolithic catalyst.BET,TEM,H_(2)-TPR,XRD,CO_(2)-TPD and TG were used to characterize the physicochemical properties of the catalyst before and after modification.The results indicated that the CO conversion rate trends of unmodified and modified Ni/Al_(2)O_(3) monolithic catalysts over 2 h were fundamentally consistent.However,the Ni/Al_(2)O_(3) catalysts modified for 2 h demonstrated significantly enhanced performance compared to those modified for 1 h.Regarding CH4 selectivity,the modified Ni/Al_(2)O_(3) catalyst exhibited markedly better performance than the unmodified Ni/Al_(2)O_(3) catalyst,confirming the enhanced methane performance of the alkali-modified Ni/Al_(2)O_(3) monolithic catalyst.Under optimized conditions(H_(2)/CO volume ratio of 3∶1,space velocity of 10000 mL/(g·h),and temperature of 400℃),the methanation performance of the Ni/Al_(2)O_(3) monolithic catalyst modified for 2 h reached its peak,achieving a CO conversion rate of 97%with 100%CH4 selectivity.