Due to native character of thermal expansion coefficient(CTE)mismatch between C_(f)/SiC and GH3536,achieving high strength joint was a huge challenge for C_(f)/SiC-GH3536 joints.Herein,a composite filler metal of Ag-C...Due to native character of thermal expansion coefficient(CTE)mismatch between C_(f)/SiC and GH3536,achieving high strength joint was a huge challenge for C_(f)/SiC-GH3536 joints.Herein,a composite filler metal of Ag-Cu-Ti+Sc_(2)(WO_(4))_(3) was developed to join C_(f)/SiC and GH3536.This work introduced Sc_(2)(WO_(4))_(3) to Ag-Cu-Ti system as a negative thermal expansion(NTE)reinforcing phase to release joint residual stress.Sc_(2)(WO_(4))_(3) was evenly distributed in the brazing seam and reacted with Ti to form Ti_(3)O_(5) reaction layer.The results of finite element analysis showed that the residual stress of the joints was effectively released by introducing Sc_(2)(WO_(4))_(3) reinforcing phase,and the mises stress was decreased from447 to 401 MPa.The maximum shear strength of the C_(f)/SiC-GH3536 joint brazed with Ag-Cu-Ti+6 vol%Sc_(2)(WO_(4))_(3) filler alloys was 64 MPa,which was about 2.6 times higher than that of Ag-Cu-Ti alloys.The results of this study provide a promising strategy for the introduction of new Sc_(2)(WO_(4))_(3) reinforcing phase in Ag-Cu-Ti system,and improve the reliability and feasibility of composite brazing alloy in brazing filed.展开更多
In order to investigate the response of cellular spacing to the variation of growth velocity under near-rapid directional solidification condition, Al-0.53wt%Zn alloy is directionally solidified with Bridgman apparatu...In order to investigate the response of cellular spacing to the variation of growth velocity under near-rapid directional solidification condition, Al-0.53wt%Zn alloy is directionally solidified with Bridgman apparatus. The results show that at the given temperature gradient the obtained microstrvctures are all cells and there exists a wide distribution range of cellular spacing. The maximum, λmax, minimum, λmin, and average cellular spacing, λ, as functions of growth rate, V, can be given by λmax=948.51V-0.4961, λmin= 661.16V-0.5015 and λ=412.41V-0.5049, respectively. The experimental results are compared with that predicted by KGT model, and a good agreement is found. Moreover,it is found that the average cellular spacing is also remarkably history-dependent.展开更多
Two low-lying unbound states in ^(16)C are investigated by deuteron inelastic scattering in inverse kinematics.Besides the 2^(-) state at 5.45 MeV previously measured in a 1n knockout reaction,a new resonant state at ...Two low-lying unbound states in ^(16)C are investigated by deuteron inelastic scattering in inverse kinematics.Besides the 2^(-) state at 5.45 MeV previously measured in a 1n knockout reaction,a new resonant state at 6.89 MeV is observed for the first time.The inelastic scattering angular distributions of these two states are well reproduced by the distorted-wave Born approximation(DWBA)calculation with an l=1 excitation.In addition,the spinparities of the unbound states are discussed and tentatively assigned based on shell model calculations using the modified YSOX interaction.展开更多
基金the National Natural Science Foundation of China(Grant Nos.51575135 and 51622503)Natural Science Foundation of Heilongjiang Province of China(YQ2019E023)。
文摘Due to native character of thermal expansion coefficient(CTE)mismatch between C_(f)/SiC and GH3536,achieving high strength joint was a huge challenge for C_(f)/SiC-GH3536 joints.Herein,a composite filler metal of Ag-Cu-Ti+Sc_(2)(WO_(4))_(3) was developed to join C_(f)/SiC and GH3536.This work introduced Sc_(2)(WO_(4))_(3) to Ag-Cu-Ti system as a negative thermal expansion(NTE)reinforcing phase to release joint residual stress.Sc_(2)(WO_(4))_(3) was evenly distributed in the brazing seam and reacted with Ti to form Ti_(3)O_(5) reaction layer.The results of finite element analysis showed that the residual stress of the joints was effectively released by introducing Sc_(2)(WO_(4))_(3) reinforcing phase,and the mises stress was decreased from447 to 401 MPa.The maximum shear strength of the C_(f)/SiC-GH3536 joint brazed with Ag-Cu-Ti+6 vol%Sc_(2)(WO_(4))_(3) filler alloys was 64 MPa,which was about 2.6 times higher than that of Ag-Cu-Ti alloys.The results of this study provide a promising strategy for the introduction of new Sc_(2)(WO_(4))_(3) reinforcing phase in Ag-Cu-Ti system,and improve the reliability and feasibility of composite brazing alloy in brazing filed.
文摘In order to investigate the response of cellular spacing to the variation of growth velocity under near-rapid directional solidification condition, Al-0.53wt%Zn alloy is directionally solidified with Bridgman apparatus. The results show that at the given temperature gradient the obtained microstrvctures are all cells and there exists a wide distribution range of cellular spacing. The maximum, λmax, minimum, λmin, and average cellular spacing, λ, as functions of growth rate, V, can be given by λmax=948.51V-0.4961, λmin= 661.16V-0.5015 and λ=412.41V-0.5049, respectively. The experimental results are compared with that predicted by KGT model, and a good agreement is found. Moreover,it is found that the average cellular spacing is also remarkably history-dependent.
基金Supported by the National Key R&D Program of China(2018YFA0404403)the National Natural Science Foundation of China(11775004,U1867214,11875074,11961141003)+1 种基金the funding from the State Key Laboratory of Nuclear Physics and Technology,Peking University(NPT2021ZZ01)the funding from Heavy Ion Research Facility in Lanzhou(HIR2021PY002)。
文摘Two low-lying unbound states in ^(16)C are investigated by deuteron inelastic scattering in inverse kinematics.Besides the 2^(-) state at 5.45 MeV previously measured in a 1n knockout reaction,a new resonant state at 6.89 MeV is observed for the first time.The inelastic scattering angular distributions of these two states are well reproduced by the distorted-wave Born approximation(DWBA)calculation with an l=1 excitation.In addition,the spinparities of the unbound states are discussed and tentatively assigned based on shell model calculations using the modified YSOX interaction.