Zinc-ion supercapacitors(ZISCs)have received considerable interest for energy storage because of their low cost,high safety,and minimal environmental impact.However,they have a low energy density and poor cycling perf...Zinc-ion supercapacitors(ZISCs)have received considerable interest for energy storage because of their low cost,high safety,and minimal environmental impact.However,they have a low energy density and poor cycling performance.The design of a better cathode material is needed to overcome these limitations.A simple method was used to synthesize binder-free electrochemically exfoliated carbon paper(EECP)which modifies the surface of the paper by introducing oxygen functional groups and thus improves its pseudocapacitance.When used in a Zn-ion supercapacitor(ZISC),an EECPbased cathode provides a large surface area and quick charge transfer.As a result,the ZISC had remarkable charge storage properties and had a dominant capacitive-type charge storage mechanism with 78.8%retention of capacity at 10 mV/s of the total storage.Furthermore,at 1 A/g,the EECP electrode had a maximum capacitance of 252.5 F/g.The EECP electrode retained 81.7%of its capacitance after 10000 cycles,indicating its promise for use in the growing renewable energy sector.A ZISC was also constructed using EECP as the positive electrode and Zn as the negative electrode with a 1 mol L^(−1) ZnSO_(4) electrolyte.It had a capacitance of 186.22 F/g at 1 A/g and a 97.01%retention rate after 10000 cycles.It also had an excellent energy density of 46.6 Wh/kg at a power density of 500.4 W/kg.The material is therefore suitable for use in high-rate next-generation ZISCs.展开更多
基金supported by National Natural Science Foundation of China(52472194)the Deanship of Research and Graduate Studies at King Khalid University through Large Research Project(RGP-2/687/46).
文摘Zinc-ion supercapacitors(ZISCs)have received considerable interest for energy storage because of their low cost,high safety,and minimal environmental impact.However,they have a low energy density and poor cycling performance.The design of a better cathode material is needed to overcome these limitations.A simple method was used to synthesize binder-free electrochemically exfoliated carbon paper(EECP)which modifies the surface of the paper by introducing oxygen functional groups and thus improves its pseudocapacitance.When used in a Zn-ion supercapacitor(ZISC),an EECPbased cathode provides a large surface area and quick charge transfer.As a result,the ZISC had remarkable charge storage properties and had a dominant capacitive-type charge storage mechanism with 78.8%retention of capacity at 10 mV/s of the total storage.Furthermore,at 1 A/g,the EECP electrode had a maximum capacitance of 252.5 F/g.The EECP electrode retained 81.7%of its capacitance after 10000 cycles,indicating its promise for use in the growing renewable energy sector.A ZISC was also constructed using EECP as the positive electrode and Zn as the negative electrode with a 1 mol L^(−1) ZnSO_(4) electrolyte.It had a capacitance of 186.22 F/g at 1 A/g and a 97.01%retention rate after 10000 cycles.It also had an excellent energy density of 46.6 Wh/kg at a power density of 500.4 W/kg.The material is therefore suitable for use in high-rate next-generation ZISCs.
