In order to improve the corrosion resistance of AZ91D magnesium alloy,a coating was formed by a potentiostatic technique from a solutions containing Ce(NO_(3))_(3),Na_(2)MoO_(4)and citric acid(H_(3)Cit).The degree of ...In order to improve the corrosion resistance of AZ91D magnesium alloy,a coating was formed by a potentiostatic technique from a solutions containing Ce(NO_(3))_(3),Na_(2)MoO_(4)and citric acid(H_(3)Cit).The degree of corrosion protection achieved was evaluated in simulated physiological solution by monitoring the open circuit potential,polarization techniques and electrochemical impedance spectroscopy(EIS).Surface analysis techniques(SEM,EDS,X-ray diffraction and X-ray photoelectron spectroscopy(XPS))were used for coating characterization.The film is mainly composed by cerium and molybdenum oxides and magnesium oxides and hydroxides.The obtained results show that the corrosion resistance of the coated electrodes has been increased significantly.This improvement in the anticorrosive performance is in part due to the corrosion inhibition properties of H_(3)Cit.展开更多
Cerium-based conversion coatings were formed on AZ91D magnesium alloy by immersion of the substrate in solutions containing Ce(NO_(3))_(3),H_(2)O_(2) and ascorbic acid(HAsc).The characterisation of the films was perfo...Cerium-based conversion coatings were formed on AZ91D magnesium alloy by immersion of the substrate in solutions containing Ce(NO_(3))_(3),H_(2)O_(2) and ascorbic acid(HAsc).The characterisation of the films was performed by electrochemical and surface analysis techniques such as SEM,EDS,X-ray diffraction and X-ray photoelectron spectroscopy(XPS).The degree of corrosion protection achieved was evaluated in simulated physiological solution by the open circuit potential monitoring,polarisation techniques and electrochemical impedance spectroscopy(EIS).The presence of HAsc in the conversion solution causes changes in the morphology,adherence and anticorrosive performance of the films.The improvement in the corrosion resistance is closely associated with the corrosion inhibition properties of HAsc.展开更多
In this work hollow rectangular microtubes of polypyrrole(PPy)films were potentiostatically electrodeposited on magnesium alloy AZ91D in salicylate solution.The substrate was previously anodized under potentiostatic c...In this work hollow rectangular microtubes of polypyrrole(PPy)films were potentiostatically electrodeposited on magnesium alloy AZ91D in salicylate solution.The substrate was previously anodized under potentiostatic conditions in a molybdate solution in order to improve the adherence of polymer.Finally the duplex film was modified by the incorporation of silver species.The obtained coatings were characterized by scanning electron microscopy(SEM),X-ray diffraction(XRD)and X-ray photoelectron spectroscopies(XPS)and the antimicrobial activity against the bacteria Escherichia coli was evaluated.The corrosion protection properties of the coatings were examined in Ringer solution by monitoring the open circuit potential,polarization techniques and electrochemical spectroscopy(EIS).The duplex coating presents an improved anticorrosive performance with respect to the PPy film.The best results concerning corrosion protection and antibacterial activity were obtained for the silver-modified composite coating.展开更多
Magnesium alloys have attracted attention due to their biocompatibility and biodegradability.In this work,composite coatings are developed to potentially improve the corrosion resistance of AZ91D Mg alloy in simulated...Magnesium alloys have attracted attention due to their biocompatibility and biodegradability.In this work,composite coatings are developed to potentially improve the corrosion resistance of AZ91D Mg alloy in simulated physiological fluid.Cerium-based/stearic acid coatings were prepared by electrodeposition combined with a simple immersion method.The effect of stearic acid bath concentration on the contact angle and corrosion resistance of the composite coatings was evaluated.The results showed that the stearic acid treatment increased the hydrophobicity of the surfaces of the cerium-based simple coatings.The use of an appropriate stearic acid concentration is a key for the fabrication of hydrophobic surfaces.The duplex coatings were demonstrated to protect the substrate from corrosion in Ringer solution.展开更多
基金CONICET(PIP-112-201101-00055)ANPCYT(PICT-2015-0726)Universidad Nacional del Sur(PGI 24/M127),Bahía Blanca,Argentina。
文摘In order to improve the corrosion resistance of AZ91D magnesium alloy,a coating was formed by a potentiostatic technique from a solutions containing Ce(NO_(3))_(3),Na_(2)MoO_(4)and citric acid(H_(3)Cit).The degree of corrosion protection achieved was evaluated in simulated physiological solution by monitoring the open circuit potential,polarization techniques and electrochemical impedance spectroscopy(EIS).Surface analysis techniques(SEM,EDS,X-ray diffraction and X-ray photoelectron spectroscopy(XPS))were used for coating characterization.The film is mainly composed by cerium and molybdenum oxides and magnesium oxides and hydroxides.The obtained results show that the corrosion resistance of the coated electrodes has been increased significantly.This improvement in the anticorrosive performance is in part due to the corrosion inhibition properties of H_(3)Cit.
基金CONICET(PIP-112-201101-00055)ANPCYT(PICT-2012-0141)and Universidad Nacional del Sur(PGI 24/M127)Bahía Blanca,Argentina are acknowledged for financial support.
文摘Cerium-based conversion coatings were formed on AZ91D magnesium alloy by immersion of the substrate in solutions containing Ce(NO_(3))_(3),H_(2)O_(2) and ascorbic acid(HAsc).The characterisation of the films was performed by electrochemical and surface analysis techniques such as SEM,EDS,X-ray diffraction and X-ray photoelectron spectroscopy(XPS).The degree of corrosion protection achieved was evaluated in simulated physiological solution by the open circuit potential monitoring,polarisation techniques and electrochemical impedance spectroscopy(EIS).The presence of HAsc in the conversion solution causes changes in the morphology,adherence and anticorrosive performance of the films.The improvement in the corrosion resistance is closely associated with the corrosion inhibition properties of HAsc.
基金CONICET(PIP-112-201101-00055),ANPCYT(PICT-2012-0141)and Universidad Nacional del Sur(PGI 24/M127),Bahía Blanca,Argentina are acknowledged for financial support
文摘In this work hollow rectangular microtubes of polypyrrole(PPy)films were potentiostatically electrodeposited on magnesium alloy AZ91D in salicylate solution.The substrate was previously anodized under potentiostatic conditions in a molybdate solution in order to improve the adherence of polymer.Finally the duplex film was modified by the incorporation of silver species.The obtained coatings were characterized by scanning electron microscopy(SEM),X-ray diffraction(XRD)and X-ray photoelectron spectroscopies(XPS)and the antimicrobial activity against the bacteria Escherichia coli was evaluated.The corrosion protection properties of the coatings were examined in Ringer solution by monitoring the open circuit potential,polarization techniques and electrochemical spectroscopy(EIS).The duplex coating presents an improved anticorrosive performance with respect to the PPy film.The best results concerning corrosion protection and antibacterial activity were obtained for the silver-modified composite coating.
基金financially supported by CONICET(No.PIP11220200102064CO)ANPCYT(No.PICT 2019–02758)+1 种基金Universidad Nacional del Sur(No.PGI 24/M159)Bahía Blanca,Argentina
文摘Magnesium alloys have attracted attention due to their biocompatibility and biodegradability.In this work,composite coatings are developed to potentially improve the corrosion resistance of AZ91D Mg alloy in simulated physiological fluid.Cerium-based/stearic acid coatings were prepared by electrodeposition combined with a simple immersion method.The effect of stearic acid bath concentration on the contact angle and corrosion resistance of the composite coatings was evaluated.The results showed that the stearic acid treatment increased the hydrophobicity of the surfaces of the cerium-based simple coatings.The use of an appropriate stearic acid concentration is a key for the fabrication of hydrophobic surfaces.The duplex coatings were demonstrated to protect the substrate from corrosion in Ringer solution.