This study investigates the susceptibility of hot cracking and weldment heat treatment of Haynes 230 superalloy. The Varestriant test was conducted to evaluate this susceptibility. Welding was performed by gas tungste...This study investigates the susceptibility of hot cracking and weldment heat treatment of Haynes 230 superalloy. The Varestriant test was conducted to evaluate this susceptibility. Welding was performed by gas tungsten arc welding （GTAW） and plasma arc welding （PAW） with stress relief heat treatment and solid solution heat treatment. A tensile test is then performed to measure the changes in the mechanical properties of the heattreated material. The results indicate that the number of thermal cycles does not affect the susceptibility of Haynes 230 superalloy to hot cracking. However, it does increase the strain. In weldment of heat treatment, stress relief annealing increases the yield strength and tensile strength of the welded parts. The section of the tensile specimens shows fibrous fractures on the welded parts, regardless of whether they are heat-treated.展开更多
In this study we conducted single V-groove butt welding （GTAW） on three types of heat treatable aluminum alloys 2024-T351, 6061-T6 and 7075-T6 and compared the angular distortion levels of the three aluminum alloys ...In this study we conducted single V-groove butt welding （GTAW） on three types of heat treatable aluminum alloys 2024-T351, 6061-T6 and 7075-T6 and compared the angular distortion levels of the three aluminum alloys at different Vee preparation angles with or without restraint. Experimental results demonstrated that when the Vee preparation angle was 0° （I-shaped groove）, the angular distortion level of the restrained weldment can exceed that of the unrestrained weldments. Moreover, when the Vee preparation angle was 45°, 60° or 90°, the restrained weldment had lower angular distortion than the unrestrained weldments. The single Vee preparation angle （amount of filler metal） in butt welding affected the angular distortion of the weldment. Without restraint, the angular distortion tended to increase with the single Vee preparation angle. Meanwhile, the angular distortion tended to decrease when the single Vee preparation angle was 60% Additionally, a restrained weldment had high angular distortion when the single Vee preparation angle was 0°. Notably, the angular distortion tended to reduce with increasing single Vee preparation angle. The angular distortion of the weldment was minimized at an angle of 60°. However, the angular distortion increased when the Vee preparation angle exceeded 60% The high-temperature yield strength of a material also affected its angular distortion. Angular distortion increased with high-temperature yield strength. Experimental results also showed that, from the strongest to the weakest, the high-temperature yield strength of the three types of aluminum alloys followed the order 6061-T6 and 2024-T351〉7075-T6.展开更多
文摘This study investigates the susceptibility of hot cracking and weldment heat treatment of Haynes 230 superalloy. The Varestriant test was conducted to evaluate this susceptibility. Welding was performed by gas tungsten arc welding （GTAW） and plasma arc welding （PAW） with stress relief heat treatment and solid solution heat treatment. A tensile test is then performed to measure the changes in the mechanical properties of the heattreated material. The results indicate that the number of thermal cycles does not affect the susceptibility of Haynes 230 superalloy to hot cracking. However, it does increase the strain. In weldment of heat treatment, stress relief annealing increases the yield strength and tensile strength of the welded parts. The section of the tensile specimens shows fibrous fractures on the welded parts, regardless of whether they are heat-treated.
文摘In this study we conducted single V-groove butt welding （GTAW） on three types of heat treatable aluminum alloys 2024-T351, 6061-T6 and 7075-T6 and compared the angular distortion levels of the three aluminum alloys at different Vee preparation angles with or without restraint. Experimental results demonstrated that when the Vee preparation angle was 0° （I-shaped groove）, the angular distortion level of the restrained weldment can exceed that of the unrestrained weldments. Moreover, when the Vee preparation angle was 45°, 60° or 90°, the restrained weldment had lower angular distortion than the unrestrained weldments. The single Vee preparation angle （amount of filler metal） in butt welding affected the angular distortion of the weldment. Without restraint, the angular distortion tended to increase with the single Vee preparation angle. Meanwhile, the angular distortion tended to decrease when the single Vee preparation angle was 60% Additionally, a restrained weldment had high angular distortion when the single Vee preparation angle was 0°. Notably, the angular distortion tended to reduce with increasing single Vee preparation angle. The angular distortion of the weldment was minimized at an angle of 60°. However, the angular distortion increased when the Vee preparation angle exceeded 60% The high-temperature yield strength of a material also affected its angular distortion. Angular distortion increased with high-temperature yield strength. Experimental results also showed that, from the strongest to the weakest, the high-temperature yield strength of the three types of aluminum alloys followed the order 6061-T6 and 2024-T351〉7075-T6.
