The possibility of applying steel slag as mineraladmixture in steam-cured concrete was investigated. Thecompressive strength, chloride permeability, carbonationdepth and drying shrinkage of concrete and the microstruc...The possibility of applying steel slag as mineraladmixture in steam-cured concrete was investigated. Thecompressive strength, chloride permeability, carbonationdepth and drying shrinkage of concrete and the microstructurecharacteristics of hardened paste were studied. Results showthat the steam-cured concrete containing steel slag at a highwater-to-binder ratio has low compressive strength, coarsepore structure, moderate permeability, large carbonation depthand great drying shrinkage. The negative effects of steel slagon the mechanical and durability performance of steam-curedconcrete become smaller at a low water-to-binder ratio or byadding ultrafine ground granulated blast furnace slag（UGGBS）. The later-age hydration of cement is significantlypromoted by adding steel slag. The pozzolanic reaction andmicro-filler effect of UGGBS result in dense structure, whichmakes great contribution to the strength development anddurability performance of steam-cured concrete. These effectsof steel slag and UGGBS are significant at a low water tobinder ratio. The steam-cured concrete containing steel slag-UGGBS blended mineral admixture at a low water-to-binderratio has the best performance with high compressive strength,fine pore structure and good durability.展开更多
Introduction The widespread use of cement in concrete leads to increased carbon emissions,so the demand for supplementary cementitious materials increases significantly.Limestone powder and steel slag powder are widel...Introduction The widespread use of cement in concrete leads to increased carbon emissions,so the demand for supplementary cementitious materials increases significantly.Limestone powder and steel slag powder are widely used as supplementary cementitious materials in modern concrete.However,for UHPC and self-compacting concrete,an extremely low water/binder(W/B)ratio is on one hand a key factor in achieving ultra-high strength and ultra-low porosity of the materials,on the other hand,also leads to the deterioration of the rheological properties of the fresh paste.Meanwhile,the existing researches focus on the influence of single limestone powder or steel slag powder on the mechanical properties or microstructure of cement-based materials.Little work on the influence of steel slag powder or limestone powder on the rheological properties of composite paste at an extremely low water/binder ratio has been investigated quantitatively.The mechanism of the effect of steel slag powder or limestone powder on the rheological properties of composite paste at extremely low water/binder ratios is still unclear.In this work,the effects of steel slag powder and limestone powder on the rheological properties of composite paste at different low water/binder ratios were analyzed via determining the flow diameter,setting time,marsh cone flow time,rheological parameters,and total organic carbon content.Methods A composite paste was prepared with P.I 42.5 ordinary Portland cement,steel slag powder,limestone powder,blast furnace slag and silica fume as raw materials in a certain proportion.To achieve the preparation of composite paste with extremely low water/binder ratios,a polycarboxylate superplasticizer with a water/reducing rate of 40%(Jiangsu Subot New Materials Co.,Ltd.,China)was used.The dosage of polycarboxylate superplasticizer for the composite paste with different water/binder ratios of 0.16 and 0.21 was 2%and 0.8%,respectively.Composite pastes with different proportions of steel slag powder or limestone powder at water/binder ratios of 0.16 and 0.21 were prepared.The flow diameter(i.e.,the larger the flow diameter,the better the fluidity),setting time(i.e.,the time when the fluidity is lost)and marsh cone flow time(i.e.,the shorter the flow time,the better the fluidity)were determined to analyze the fluidity of the composite pastes.the rheological properties of composite paste at a water/binder ratio of 0.16 for rheological properties tests were determined,and the rheological parameters were obtained by the H-B model.The adsorption performance of the polycarboxylate superplasticizer was analyzed by testing the TOC content.Results and discussion When the ratio of water/binder is 0.16,both limestone powder and steel slag powder initially increase the flow diameter of the composite paste.However,the fluidity of the composite paste decreases over time,and the reduction is more pronounced with steel slag powder.This is because the nucleation and hydration promotion effect of limestone powder can reduce the loss rate of flow diameter,while the rough particles of steel slag powder increase the internal friction force,resulting in a decrease in the flow diameter of composite paste.Adding limestone powder and steel slag powder both shortens the setting time and marsh cone flow time of the composite paste.However,the steel slag powder addition of 30%delays the final setting time due to its delaying effect.Also,limestone powder can enhance the thixotropy and reduce the yield stress and plastic viscosity,thereby improving the rheological properties.In contrast,steel slag powder can increase the yield stress and plastic viscosity,thereby weakening the rheological properties and thixotropy.Steel slag powder and limestone powder both can enhance the adsorption effect of polycarboxylate superplasticizer.Steel slag powder has a stronger adsorption effect.The composite paste containing limestone powder has a higher free water content.This is because the rough and porous surface of steel slag itself and the uneven particle shape lead to the physical adsorption of polycarboxylate superplasticizer molecules on the surface of steel slag particles,thereby reducing the effective content of the water reducer dispersion.Increasing the water/binder ratio to 0.21 results in a decrease in the flow diameter of the composite paste.Furthermore,the setting time and marsh cone flow time can prolong due to the reduction in the dosage of polycarboxylate superplasticizer.Conclusions The results showed that the fluidity loss rate of composite paste with limestone powder could be lower than that of composite paste with steel slag powder.Compared to steel slag powder,the addition of limestone powder reduced the setting time and marsh cone flow time of the composite paste.The addition of limestone powder could shorten the yield stress and plastic viscosity of the composite paste.Therefore,the composite paste with limestone powder had better rheological properties and stronger thixotropy rather than that with steel slag powder.The addition of limestone powder could improve the rheological properties of the composite paste.Compared to composite paste with limestone powder,a better adsorption effect of polycarboxylate superplasticizer on the surface of the composite binder with steel slag powder could be obtained.The free water content of the composite paste with limestone powder was still higher than that of the composite paste with steel slag powder.The fluidity and rheological properties of the composite paste with limestone powder could be better.The comprehensive analysis indicated that a positive effect of limestone powder on rheological properties of composite paste at an extremely low water/binder ratio could be more dominant than that of steel slag powder.展开更多
The characteristics of C-S-H gel in hardened Portland cement pastes and complex binder pastes with ground granulated blast furnace slag were investigated with nanoindentation. The composition of C-S-H gel was analysed...The characteristics of C-S-H gel in hardened Portland cement pastes and complex binder pastes with ground granulated blast furnace slag were investigated with nanoindentation. The composition of C-S-H gel was analysed with SEM-EDS. The obtained results showed that the volume fraction of LD C-S-H gradually reduced and the volume fraction of HD C-S-H increased with the prolongation of hydration age. Most of the C-S-H gel produced at later age was HD C-S-H. The volume fraction of HD C-S-H increased as the fraction of slag in complex binder pastes increased, suggesting that HD C-S-H was mainly in the hydration products of slag. The chemichal compositions of the two types of C-S-H gel were simlar, meaning that formation and transformation of the two types of C-S-H gel were not affected by their Ca/Si ratio.展开更多
基金Postdoctoral Science Foundation of China(No.2015M580992,2016T90036)the Open Fund of State Key Laboratory of High Performance Civil Engineering Materials(No.2015CEM010)
文摘The possibility of applying steel slag as mineraladmixture in steam-cured concrete was investigated. Thecompressive strength, chloride permeability, carbonationdepth and drying shrinkage of concrete and the microstructurecharacteristics of hardened paste were studied. Results showthat the steam-cured concrete containing steel slag at a highwater-to-binder ratio has low compressive strength, coarsepore structure, moderate permeability, large carbonation depthand great drying shrinkage. The negative effects of steel slagon the mechanical and durability performance of steam-curedconcrete become smaller at a low water-to-binder ratio or byadding ultrafine ground granulated blast furnace slag（UGGBS）. The later-age hydration of cement is significantlypromoted by adding steel slag. The pozzolanic reaction andmicro-filler effect of UGGBS result in dense structure, whichmakes great contribution to the strength development anddurability performance of steam-cured concrete. These effectsof steel slag and UGGBS are significant at a low water tobinder ratio. The steam-cured concrete containing steel slag-UGGBS blended mineral admixture at a low water-to-binderratio has the best performance with high compressive strength,fine pore structure and good durability.
文摘Introduction The widespread use of cement in concrete leads to increased carbon emissions,so the demand for supplementary cementitious materials increases significantly.Limestone powder and steel slag powder are widely used as supplementary cementitious materials in modern concrete.However,for UHPC and self-compacting concrete,an extremely low water/binder(W/B)ratio is on one hand a key factor in achieving ultra-high strength and ultra-low porosity of the materials,on the other hand,also leads to the deterioration of the rheological properties of the fresh paste.Meanwhile,the existing researches focus on the influence of single limestone powder or steel slag powder on the mechanical properties or microstructure of cement-based materials.Little work on the influence of steel slag powder or limestone powder on the rheological properties of composite paste at an extremely low water/binder ratio has been investigated quantitatively.The mechanism of the effect of steel slag powder or limestone powder on the rheological properties of composite paste at extremely low water/binder ratios is still unclear.In this work,the effects of steel slag powder and limestone powder on the rheological properties of composite paste at different low water/binder ratios were analyzed via determining the flow diameter,setting time,marsh cone flow time,rheological parameters,and total organic carbon content.Methods A composite paste was prepared with P.I 42.5 ordinary Portland cement,steel slag powder,limestone powder,blast furnace slag and silica fume as raw materials in a certain proportion.To achieve the preparation of composite paste with extremely low water/binder ratios,a polycarboxylate superplasticizer with a water/reducing rate of 40%(Jiangsu Subot New Materials Co.,Ltd.,China)was used.The dosage of polycarboxylate superplasticizer for the composite paste with different water/binder ratios of 0.16 and 0.21 was 2%and 0.8%,respectively.Composite pastes with different proportions of steel slag powder or limestone powder at water/binder ratios of 0.16 and 0.21 were prepared.The flow diameter(i.e.,the larger the flow diameter,the better the fluidity),setting time(i.e.,the time when the fluidity is lost)and marsh cone flow time(i.e.,the shorter the flow time,the better the fluidity)were determined to analyze the fluidity of the composite pastes.the rheological properties of composite paste at a water/binder ratio of 0.16 for rheological properties tests were determined,and the rheological parameters were obtained by the H-B model.The adsorption performance of the polycarboxylate superplasticizer was analyzed by testing the TOC content.Results and discussion When the ratio of water/binder is 0.16,both limestone powder and steel slag powder initially increase the flow diameter of the composite paste.However,the fluidity of the composite paste decreases over time,and the reduction is more pronounced with steel slag powder.This is because the nucleation and hydration promotion effect of limestone powder can reduce the loss rate of flow diameter,while the rough particles of steel slag powder increase the internal friction force,resulting in a decrease in the flow diameter of composite paste.Adding limestone powder and steel slag powder both shortens the setting time and marsh cone flow time of the composite paste.However,the steel slag powder addition of 30%delays the final setting time due to its delaying effect.Also,limestone powder can enhance the thixotropy and reduce the yield stress and plastic viscosity,thereby improving the rheological properties.In contrast,steel slag powder can increase the yield stress and plastic viscosity,thereby weakening the rheological properties and thixotropy.Steel slag powder and limestone powder both can enhance the adsorption effect of polycarboxylate superplasticizer.Steel slag powder has a stronger adsorption effect.The composite paste containing limestone powder has a higher free water content.This is because the rough and porous surface of steel slag itself and the uneven particle shape lead to the physical adsorption of polycarboxylate superplasticizer molecules on the surface of steel slag particles,thereby reducing the effective content of the water reducer dispersion.Increasing the water/binder ratio to 0.21 results in a decrease in the flow diameter of the composite paste.Furthermore,the setting time and marsh cone flow time can prolong due to the reduction in the dosage of polycarboxylate superplasticizer.Conclusions The results showed that the fluidity loss rate of composite paste with limestone powder could be lower than that of composite paste with steel slag powder.Compared to steel slag powder,the addition of limestone powder reduced the setting time and marsh cone flow time of the composite paste.The addition of limestone powder could shorten the yield stress and plastic viscosity of the composite paste.Therefore,the composite paste with limestone powder had better rheological properties and stronger thixotropy rather than that with steel slag powder.The addition of limestone powder could improve the rheological properties of the composite paste.Compared to composite paste with limestone powder,a better adsorption effect of polycarboxylate superplasticizer on the surface of the composite binder with steel slag powder could be obtained.The free water content of the composite paste with limestone powder was still higher than that of the composite paste with steel slag powder.The fluidity and rheological properties of the composite paste with limestone powder could be better.The comprehensive analysis indicated that a positive effect of limestone powder on rheological properties of composite paste at an extremely low water/binder ratio could be more dominant than that of steel slag powder.
基金supported by the National Basic Research Program of China ("973" Project) (Grant No. 2009CB623106)the National Natural Science Foundation of China (Grant No. U1134008)
文摘The characteristics of C-S-H gel in hardened Portland cement pastes and complex binder pastes with ground granulated blast furnace slag were investigated with nanoindentation. The composition of C-S-H gel was analysed with SEM-EDS. The obtained results showed that the volume fraction of LD C-S-H gradually reduced and the volume fraction of HD C-S-H increased with the prolongation of hydration age. Most of the C-S-H gel produced at later age was HD C-S-H. The volume fraction of HD C-S-H increased as the fraction of slag in complex binder pastes increased, suggesting that HD C-S-H was mainly in the hydration products of slag. The chemichal compositions of the two types of C-S-H gel were simlar, meaning that formation and transformation of the two types of C-S-H gel were not affected by their Ca/Si ratio.