The relationship of hydrogen, GBF （granular bright facet） and very high cycle fatigue properties of high strength spring steels 60Si2CrV with three different hydrogen contents were studied using hydrogen thermal des...The relationship of hydrogen, GBF （granular bright facet） and very high cycle fatigue properties of high strength spring steels 60Si2CrV with three different hydrogen contents were studied using hydrogen thermal desorp- tion analysis and ultrasonic fatigue test. The results showed that the influence of hydrogen on the relationship between fatigue life and the ratio of GBF to inclusion size was obvious, and the expression between fatigue life and with different hydrogen contents can also be obtained. In addition, based on the research of hydrogen diffusion and GBF, it was explained why the GBF cannot form below 106 cycles. At last, the estimated critical fa tigue life of GBF formation can be expressed accurately.展开更多
Non-quenched and tempered(NQT)steels have been applied for auto forging products at the aim of lower cost since 1980’s in China.Without quenching and tempering processes,the cost of heat treatment was greatly decreas...Non-quenched and tempered(NQT)steels have been applied for auto forging products at the aim of lower cost since 1980’s in China.Without quenching and tempering processes,the cost of heat treatment was greatly decreased,so they are widely applied in car forgings such as crankshaft,connecting rod.Recently,with the aim of improving performance and reducing production cost,new technologies,such as:reductions of microalloyed elements,microstructure refining,and mechanical properties forecast have been developed in China auto industry.The designation,processing,properties prediction and microstructure of auto components have been controlled comprehensively.With the development of new technologies,NQT steel gradually began to be applied to product important parts,and replace Quenching and Tempering(QT)steels.Both steel makers and end product users are expressed their desire to share benefits of technological innovation.The technologies will have a huge developing space and very bright developing prospects in motor parts industry in future.展开更多
The steel specimens of nominal composition 0.3C-1.0Cr-1.0Mn-2.0Si-1.0Ni-0.04 Nb were quenched and tempered or isothermally quenched from various temperatures.It is found that the steel quenched and tempered with a ten...The steel specimens of nominal composition 0.3C-1.0Cr-1.0Mn-2.0Si-1.0Ni-0.04 Nb were quenched and tempered or isothermally quenched from various temperatures.It is found that the steel quenched and tempered with a tensile strength of 1 500-1 600 MPa has a KISCC（critical stress intensity factor） value below 15.0 MPa · m1/2.The steel isothermally quenched with a tensile strength of 1 350-1 750 MPa has a KISCC value about 20.0 MPa·m1/2.In addition,with increase of isothermal quenching temperature,the tensile strength decreases greatly and KISCC value does not pronouncedly change.The microstructure of isothermally quenched specimens is composed of bainite and retained austenite.The delayed fracture resistance is dependent on the stability of austenite,which is in turn related to the retained austenite volume fraction and carbon content in austenite.展开更多
By the increase in Mo content,the addition of microalloying elements V and Nb and by reducing the contents of Mn,P and S based on the composition of steel 42 CrMo,we have developed a 1 300 MPa-grade high strength stee...By the increase in Mo content,the addition of microalloying elements V and Nb and by reducing the contents of Mn,P and S based on the composition of steel 42 CrMo,we have developed a 1 300 MPa-grade high strength steel(ADF1)for bolts.The sustained load bending test,sustained load tensile test and stress corrosion cracking test have been carried out to evaluate the delayed fracture resistance of steel ADFl and commercial steel 42 CrMo.The results showed that steel ADF1 has superior delayed fracture resistance to that of 42 CrMo steel.It's concluded that the superior delayed fracture resistance of ADF1 is mainly due to the increase of tempering temperature,fine homogeneously distributed MC carbide and fine prior austenite grain size.展开更多
The delayed fracture behavior of medium carbon high strength spring steel containing different amounts of boron （0. 000 5%, 0. 001 6 %） was studied using sustained load delayed fracture test. The results show that d...The delayed fracture behavior of medium carbon high strength spring steel containing different amounts of boron （0. 000 5%, 0. 001 6 %） was studied using sustained load delayed fracture test. The results show that delayed fracture resistance of boron containing steels is higher than that of conventional steel 60Si2MnA at the same strength level and it increases with the increase of boron eontent from 0. 000 5% to 0. 001 6%. The delayed fracture mode is mainly intergranular in the boron containing steels tempered at 350℃, which indicates that the addition of boron does not change the fracture character. However, the increase of boron content enlarges the size of the crack initia tion area. Further study of phase analysis indicates that most boron is in solid solution, and only a very small quantity of boron is in the M3 （C, B） phase.展开更多
The delayed fracture behaviors of CrMo-type high strength steels containing different amount of titanium(0to 0.10%)were studied.The steels were quenched at 880℃ and tempered from 400℃ to 650℃,and a wide range of te...The delayed fracture behaviors of CrMo-type high strength steels containing different amount of titanium(0to 0.10%)were studied.The steels were quenched at 880℃ and tempered from 400℃ to 650℃,and a wide range of tensile strength was obtained.The sustained load tensile test was carried out by using notched tensile specimens in Walpole solution.The experimental results showed that with higher strength,the Ti-microalloyed steels show higher resistance to delayed fracture compared with non-microalloyed steel due to titanium beneficial role and microstructure changes.The undissolved TiC is uniformly distributed as strong hydrogen traps,retarding or preventing the diffusion and accumulation of hydrogen to lower-interaction energy sites,such as prior austenite and martensite lath boundaries in stress concentration area.Meanwhile,the grain refining effect of titanium is also an important factor to improve the delayed fracture resistance of Ti-microalloyed steels.The characteristics of delayed fracture remain nearly the same with titanium addition.展开更多
The threshold stress intensity of stress corrosion cracking(SCC) for 40 CrMo steel in 3.5%NaCl solution decreased exponentially with the increase of yield strength.The threshold stress intensity of hydrogen-induced cr...The threshold stress intensity of stress corrosion cracking(SCC) for 40 CrMo steel in 3.5%NaCl solution decreased exponentially with the increase of yield strength.The threshold stress intensity of hydrogen-induced cracking during dynamical charging for 40 CrMo steel decreased linearly with the logarithm of the concentration of diffusible hydrogen.This equation was also applicable to SCC of high strength steel in aqueous solution.The critical hydrogen enrichment concentration necessary for SCC of high strength steel in water decreased exponentially with the increase of yield strength.Based on the results,the relationship between K_(ISCC) and σ_(ys) could be deduced.展开更多
文摘The relationship of hydrogen, GBF （granular bright facet） and very high cycle fatigue properties of high strength spring steels 60Si2CrV with three different hydrogen contents were studied using hydrogen thermal desorp- tion analysis and ultrasonic fatigue test. The results showed that the influence of hydrogen on the relationship between fatigue life and the ratio of GBF to inclusion size was obvious, and the expression between fatigue life and with different hydrogen contents can also be obtained. In addition, based on the research of hydrogen diffusion and GBF, it was explained why the GBF cannot form below 106 cycles. At last, the estimated critical fa tigue life of GBF formation can be expressed accurately.
文摘Non-quenched and tempered(NQT)steels have been applied for auto forging products at the aim of lower cost since 1980’s in China.Without quenching and tempering processes,the cost of heat treatment was greatly decreased,so they are widely applied in car forgings such as crankshaft,connecting rod.Recently,with the aim of improving performance and reducing production cost,new technologies,such as:reductions of microalloyed elements,microstructure refining,and mechanical properties forecast have been developed in China auto industry.The designation,processing,properties prediction and microstructure of auto components have been controlled comprehensively.With the development of new technologies,NQT steel gradually began to be applied to product important parts,and replace Quenching and Tempering(QT)steels.Both steel makers and end product users are expressed their desire to share benefits of technological innovation.The technologies will have a huge developing space and very bright developing prospects in motor parts industry in future.
基金Item Sponsored by National Key Fundamental Research and Development Programme of China(G1998061503)
文摘The steel specimens of nominal composition 0.3C-1.0Cr-1.0Mn-2.0Si-1.0Ni-0.04 Nb were quenched and tempered or isothermally quenched from various temperatures.It is found that the steel quenched and tempered with a tensile strength of 1 500-1 600 MPa has a KISCC（critical stress intensity factor） value below 15.0 MPa · m1/2.The steel isothermally quenched with a tensile strength of 1 350-1 750 MPa has a KISCC value about 20.0 MPa·m1/2.In addition,with increase of isothermal quenching temperature,the tensile strength decreases greatly and KISCC value does not pronouncedly change.The microstructure of isothermally quenched specimens is composed of bainite and retained austenite.The delayed fracture resistance is dependent on the stability of austenite,which is in turn related to the retained austenite volume fraction and carbon content in austenite.
基金Sponsored by National Key Fundamental Research Project(G1998061503)
文摘By the increase in Mo content,the addition of microalloying elements V and Nb and by reducing the contents of Mn,P and S based on the composition of steel 42 CrMo,we have developed a 1 300 MPa-grade high strength steel(ADF1)for bolts.The sustained load bending test,sustained load tensile test and stress corrosion cracking test have been carried out to evaluate the delayed fracture resistance of steel ADFl and commercial steel 42 CrMo.The results showed that steel ADF1 has superior delayed fracture resistance to that of 42 CrMo steel.It's concluded that the superior delayed fracture resistance of ADF1 is mainly due to the increase of tempering temperature,fine homogeneously distributed MC carbide and fine prior austenite grain size.
基金Item Sponsored by National Key Fundamental Research and Development Programme of China (2004CB619104)
文摘The delayed fracture behavior of medium carbon high strength spring steel containing different amounts of boron （0. 000 5%, 0. 001 6 %） was studied using sustained load delayed fracture test. The results show that delayed fracture resistance of boron containing steels is higher than that of conventional steel 60Si2MnA at the same strength level and it increases with the increase of boron eontent from 0. 000 5% to 0. 001 6%. The delayed fracture mode is mainly intergranular in the boron containing steels tempered at 350℃, which indicates that the addition of boron does not change the fracture character. However, the increase of boron content enlarges the size of the crack initia tion area. Further study of phase analysis indicates that most boron is in solid solution, and only a very small quantity of boron is in the M3 （C, B） phase.
文摘The delayed fracture behaviors of CrMo-type high strength steels containing different amount of titanium(0to 0.10%)were studied.The steels were quenched at 880℃ and tempered from 400℃ to 650℃,and a wide range of tensile strength was obtained.The sustained load tensile test was carried out by using notched tensile specimens in Walpole solution.The experimental results showed that with higher strength,the Ti-microalloyed steels show higher resistance to delayed fracture compared with non-microalloyed steel due to titanium beneficial role and microstructure changes.The undissolved TiC is uniformly distributed as strong hydrogen traps,retarding or preventing the diffusion and accumulation of hydrogen to lower-interaction energy sites,such as prior austenite and martensite lath boundaries in stress concentration area.Meanwhile,the grain refining effect of titanium is also an important factor to improve the delayed fracture resistance of Ti-microalloyed steels.The characteristics of delayed fracture remain nearly the same with titanium addition.
基金Item Sponsored by Special Funds for State Major Basis Research(G19990650)
文摘The threshold stress intensity of stress corrosion cracking(SCC) for 40 CrMo steel in 3.5%NaCl solution decreased exponentially with the increase of yield strength.The threshold stress intensity of hydrogen-induced cracking during dynamical charging for 40 CrMo steel decreased linearly with the logarithm of the concentration of diffusible hydrogen.This equation was also applicable to SCC of high strength steel in aqueous solution.The critical hydrogen enrichment concentration necessary for SCC of high strength steel in water decreased exponentially with the increase of yield strength.Based on the results,the relationship between K_(ISCC) and σ_(ys) could be deduced.