Hypereutectic Al -27Si alloys were joined without flux by ultrasonic-assisted soldering at 420 ℃ in air using Zn -5Al the filler alloys, and Si particulate-reinforced Zn - Al based composites filler joints were obtai...Hypereutectic Al -27Si alloys were joined without flux by ultrasonic-assisted soldering at 420 ℃ in air using Zn -5Al the filler alloys, and Si particulate-reinforced Zn - Al based composites filler joints were obtained. The ultrasonic vibration introduced into soldering could influence the migration of Si particles and the microstructure of solidified Zn - Al based alloys. Both the distribution of Si particles and microstructure of the solidified Zn - Al based alloys affected the shear strength of joints. The shear strength increased with the ultrasonic vibration time. The highest average shear strength of joints reached to -68.5 MPa. Transcrystalline rupture mode was observed on the fracture surface.展开更多
基金sponsored by the National Natural Science Foundation of China(Grant No.51504165)the Project funded by the China Postdoctoral Science Foundation(Grant No.2016M601271)Tianjin Scince&Technology Project(Grant No.16JCQNJC02600)
文摘Hypereutectic Al -27Si alloys were joined without flux by ultrasonic-assisted soldering at 420 ℃ in air using Zn -5Al the filler alloys, and Si particulate-reinforced Zn - Al based composites filler joints were obtained. The ultrasonic vibration introduced into soldering could influence the migration of Si particles and the microstructure of solidified Zn - Al based alloys. Both the distribution of Si particles and microstructure of the solidified Zn - Al based alloys affected the shear strength of joints. The shear strength increased with the ultrasonic vibration time. The highest average shear strength of joints reached to -68.5 MPa. Transcrystalline rupture mode was observed on the fracture surface.