TiN/CrN multilayered hard coatings with TiCrN interlayer were deposited onhigh speed steel substrates by using a filtered cathodic vacuum arc technique. The structure andcomposition of the coatings were characterized ...TiN/CrN multilayered hard coatings with TiCrN interlayer were deposited onhigh speed steel substrates by using a filtered cathodic vacuum arc technique. The structure andcomposition of the coatings were characterized by scanning electron microscopy (SEM) and Augerelectron spectroscopy (AES). A high adhesion of up to 80 N was demonstrated by scratching tests forthe multi-layered coatings. Nanoindentation tests were performed to determine the hardness andelastic modulus of the coatings as a function of the multiplayer modulation period. It was observedthat the hardness of the multilayered coatings is higher than those of either TiN or CrN singlecoatings, and it increases with decreasing modulation periods, which is consistent with predictionsfrom the Hall-Petch type strengthening mechanism, though at small modulation periods, deviation fromthe Hall-Petch relation has been observed for the multilayered coatings. The life-span of drillscoated with TiN/CrN multilayered is triple as long as that coated with TiN layer.展开更多
基金This work was financially supported by the Science Foundation of Lanzhou Institute Chemistry and Physics, Chinese Academy of Science (No.01-03).
文摘TiN/CrN multilayered hard coatings with TiCrN interlayer were deposited onhigh speed steel substrates by using a filtered cathodic vacuum arc technique. The structure andcomposition of the coatings were characterized by scanning electron microscopy (SEM) and Augerelectron spectroscopy (AES). A high adhesion of up to 80 N was demonstrated by scratching tests forthe multi-layered coatings. Nanoindentation tests were performed to determine the hardness andelastic modulus of the coatings as a function of the multiplayer modulation period. It was observedthat the hardness of the multilayered coatings is higher than those of either TiN or CrN singlecoatings, and it increases with decreasing modulation periods, which is consistent with predictionsfrom the Hall-Petch type strengthening mechanism, though at small modulation periods, deviation fromthe Hall-Petch relation has been observed for the multilayered coatings. The life-span of drillscoated with TiN/CrN multilayered is triple as long as that coated with TiN layer.