We took Co_(0.2)Ni_(0.8)-MOF-74 with bimetallic synergistic effect as the basic material,and selected rare earth ions Ho,Gd,and Er with ion radii close to Co and Ni as the research objects for doping.The influence of ...We took Co_(0.2)Ni_(0.8)-MOF-74 with bimetallic synergistic effect as the basic material,and selected rare earth ions Ho,Gd,and Er with ion radii close to Co and Ni as the research objects for doping.The influence of rare earth ion doping amount and doping type on the eNRR performance of the catalyst was explored.The experimental results show that the ammonia yield rate and Faraday efficiency doped with Co_(0.2)Ni_(0.8)-MOF-0.5Ho are the highest,reaching 1.28×10^(-10)mol·s^(-1)·cm^(-2)/39.8%,which is higher than the1.12×10^(-10)mol·s^(-1)·cm^(-2)/32.2%of Co_(0.2)Ni_(0.8)-MOF-74,and is about 14.3%/23.7%higher than that without doping,respectively.And the stability of Co_(0.2)Ni_(0.8)-MOF-0.5 Ho is good(after 80 hours of continuous testing,the current density did not significantly decrease).This is mainly due to doping,which gives Co_(0.2)Ni_(0.8)-MOF-74 a larger specific surface area and catalytic active sites.The catalyst doped at the same time has more metal cation centers,which increases the electron density of the metal centers and enhances the corresponding eNRR performance.展开更多
Ultrasmall near-monodisperse Ba2ErF7 nanocrystals with average crystal size 9.6 nm were synthesized with solvothermal method. The X-ray diffraction （XRD） and transmission electron microscopy （TEM） assays reveal th...Ultrasmall near-monodisperse Ba2ErF7 nanocrystals with average crystal size 9.6 nm were synthesized with solvothermal method. The X-ray diffraction （XRD） and transmission electron microscopy （TEM） assays reveal that the as-synthesized Ba2ErF7 nanocrystals are of the cubic structure with the cell parameter of 5.943 A, instead of the reported orthorhombic and tetragonal structure. Two emission bands originated from 2Hwj4H3/2 → 4F5/2 and 4F9/2 ----＋ 4115,2 of Er3＋ can be observed under a 980 nm laser excitation. The magnetic mass susceptibility of the as-synthesized BazErF7 nanocrystals reaches 4.293 × 10-5 emu g-1 Oe-1.展开更多
基金Funded by the Central Government Guides Local Funds for Scientific and Technological Development(No.2023ZYQ004)the Hunan Provincial Natural Science Foundation of China(No.2021JJ50036)the Hunan Provincial Key Research and Development Plan(No.2023GK2083)。
文摘We took Co_(0.2)Ni_(0.8)-MOF-74 with bimetallic synergistic effect as the basic material,and selected rare earth ions Ho,Gd,and Er with ion radii close to Co and Ni as the research objects for doping.The influence of rare earth ion doping amount and doping type on the eNRR performance of the catalyst was explored.The experimental results show that the ammonia yield rate and Faraday efficiency doped with Co_(0.2)Ni_(0.8)-MOF-0.5Ho are the highest,reaching 1.28×10^(-10)mol·s^(-1)·cm^(-2)/39.8%,which is higher than the1.12×10^(-10)mol·s^(-1)·cm^(-2)/32.2%of Co_(0.2)Ni_(0.8)-MOF-74,and is about 14.3%/23.7%higher than that without doping,respectively.And the stability of Co_(0.2)Ni_(0.8)-MOF-0.5 Ho is good(after 80 hours of continuous testing,the current density did not significantly decrease).This is mainly due to doping,which gives Co_(0.2)Ni_(0.8)-MOF-74 a larger specific surface area and catalytic active sites.The catalyst doped at the same time has more metal cation centers,which increases the electron density of the metal centers and enhances the corresponding eNRR performance.
文摘Ultrasmall near-monodisperse Ba2ErF7 nanocrystals with average crystal size 9.6 nm were synthesized with solvothermal method. The X-ray diffraction （XRD） and transmission electron microscopy （TEM） assays reveal that the as-synthesized Ba2ErF7 nanocrystals are of the cubic structure with the cell parameter of 5.943 A, instead of the reported orthorhombic and tetragonal structure. Two emission bands originated from 2Hwj4H3/2 → 4F5/2 and 4F9/2 ----＋ 4115,2 of Er3＋ can be observed under a 980 nm laser excitation. The magnetic mass susceptibility of the as-synthesized BazErF7 nanocrystals reaches 4.293 × 10-5 emu g-1 Oe-1.