The coating of Ni W P was deposited as base layer, and then the composite coating of Ni Ti(particles) Re(rare earth) was deposited subsequently on the surface of diamond using electroless plating by adding 2...The coating of Ni W P was deposited as base layer, and then the composite coating of Ni Ti(particles) Re(rare earth) was deposited subsequently on the surface of diamond using electroless plating by adding 2～3 μm Ti particles and trace rare earth salt to bath solution. Ti particles deposited on the surface of diamond were found by SEM and formation of TiC was verified by X ray diffraction analysis after heat treatment of the coatings in vacuum at 900 ℃. The binding strength between the coated diamond and the metal matrix was improved effectively in the diamond composite based on metal cement.展开更多
文摘The coating of Ni W P was deposited as base layer, and then the composite coating of Ni Ti(particles) Re(rare earth) was deposited subsequently on the surface of diamond using electroless plating by adding 2～3 μm Ti particles and trace rare earth salt to bath solution. Ti particles deposited on the surface of diamond were found by SEM and formation of TiC was verified by X ray diffraction analysis after heat treatment of the coatings in vacuum at 900 ℃. The binding strength between the coated diamond and the metal matrix was improved effectively in the diamond composite based on metal cement.