The centrifugal casting of compound HSS/nodular cast iron roll collar was studied,and the factors affecting transition zone quality were analyzed.The pouring temperature and interval in pouring are the main factors af...The centrifugal casting of compound HSS/nodular cast iron roll collar was studied,and the factors affecting transition zone quality were analyzed.The pouring temperature and interval in pouring are the main factors affecting transition zone quality.By controlling process parameter and flux adding during casting,high quality roll collar was obtained.The cause,why in the casting of HSS part,segregation appears easily,was analyzed and the countermeasure eliminating segregation was put forward,the measure eliminating heat treatment crackling was also put forward.展开更多
The paper has studied the mechanical properties and heat treatment effects on multi-element low alloy wear-resistant steel (MLAWS) used as a material for the liner of rolling mill torii. The results show that when que...The paper has studied the mechanical properties and heat treatment effects on multi-element low alloy wear-resistant steel (MLAWS) used as a material for the liner of rolling mill torii. The results show that when quenched at 900-920℃ and tempered at 350-370℃, the MLAWS has achieved hardness above 60 HRC, tensile strength greater than 1 600 MPa, impact toughness higher than 18J/cm2 and fracture toughness greater than 37 MPa·m1/2. When the quenching temperature is lower than 900℃, the hardness of the MLAWS increases with the temperature. When the quenching temperature is higher than 900℃, the hardness decreases with the increase of temperature. At a quenching temperature below 920℃, the effect of quenching temperature on the impact toughness is not obvious. In quenching at above 920℃, impact toughness decreases as the temperature increases. When the tempering temperature is exceeding 450℃, the hardness begins to decrease significantly. Tempering at 350℃ has produced the best wear resistance on the MLAWS.展开更多
The surface roughness of reflow conductor roll was checked on membrane sample. The surface morphology of conductor roll was observed by microscope, and the composition of adhered layer on conductor roll surface was an...The surface roughness of reflow conductor roll was checked on membrane sample. The surface morphology of conductor roll was observed by microscope, and the composition of adhered layer on conductor roll surface was analyzed by X-ray spectroscope. The results show that tin adhesion is the main reason for failure of conductor roll, and the failure of conductor roll is accelerated by wear. The measures to decrease tin adhesion and improve wear resistance were put forward.展开更多
文摘The centrifugal casting of compound HSS/nodular cast iron roll collar was studied,and the factors affecting transition zone quality were analyzed.The pouring temperature and interval in pouring are the main factors affecting transition zone quality.By controlling process parameter and flux adding during casting,high quality roll collar was obtained.The cause,why in the casting of HSS part,segregation appears easily,was analyzed and the countermeasure eliminating segregation was put forward,the measure eliminating heat treatment crackling was also put forward.
文摘The paper has studied the mechanical properties and heat treatment effects on multi-element low alloy wear-resistant steel (MLAWS) used as a material for the liner of rolling mill torii. The results show that when quenched at 900-920℃ and tempered at 350-370℃, the MLAWS has achieved hardness above 60 HRC, tensile strength greater than 1 600 MPa, impact toughness higher than 18J/cm2 and fracture toughness greater than 37 MPa·m1/2. When the quenching temperature is lower than 900℃, the hardness of the MLAWS increases with the temperature. When the quenching temperature is higher than 900℃, the hardness decreases with the increase of temperature. At a quenching temperature below 920℃, the effect of quenching temperature on the impact toughness is not obvious. In quenching at above 920℃, impact toughness decreases as the temperature increases. When the tempering temperature is exceeding 450℃, the hardness begins to decrease significantly. Tempering at 350℃ has produced the best wear resistance on the MLAWS.
文摘The surface roughness of reflow conductor roll was checked on membrane sample. The surface morphology of conductor roll was observed by microscope, and the composition of adhered layer on conductor roll surface was analyzed by X-ray spectroscope. The results show that tin adhesion is the main reason for failure of conductor roll, and the failure of conductor roll is accelerated by wear. The measures to decrease tin adhesion and improve wear resistance were put forward.