A kind of CWAO catalyst, RuO_2/γ-Al_2O_3, was prepared by dipping Al_2O_3into the aqueous solution of RuCl_3·3H_2O. XRD, SEM and TEM were used to determine the catalyticstructure. Influences of the calcination t...A kind of CWAO catalyst, RuO_2/γ-Al_2O_3, was prepared by dipping Al_2O_3into the aqueous solution of RuCl_3·3H_2O. XRD, SEM and TEM were used to determine the catalyticstructure. Influences of the calcination temperature, the initial pH of the feed solution anddegradation temperature on the activity of the RuO_2/γ-Al_2O_3 catalyst were investigated and thereaction mechanism was preliminarily studied. Results showed that uniform dispersion of RuO_2crystallites was observed on the surface of the catalyst. The activity of the catalyst was higher atcalcination temperature of 300℃ for 3 h and the particle reunion occurred and some large RuO_2crystallites were abundant at high calcination temperature of 500℃ The activity of the catalyst wasbetter in the acid solution than in the alkaline solution. Increasing degradation temperature andusing the catalyst could shorten the induction periods so that the phenol and COD removal wereincreased. For RuO_2/γ-Al_2O_3 catalyst, the phenol and COD removal were respectively 98% and 80%in a temperature of 150℃, pH of 5.6 and pressure of 3 MPa after a 2 h reaction. This indicated thatRu/γ-Al_2O_3 catalyst had good activity.展开更多
基金This project is supported by the Natural High Tech. R&D Program of China (No. 2002AA601260)
文摘A kind of CWAO catalyst, RuO_2/γ-Al_2O_3, was prepared by dipping Al_2O_3into the aqueous solution of RuCl_3·3H_2O. XRD, SEM and TEM were used to determine the catalyticstructure. Influences of the calcination temperature, the initial pH of the feed solution anddegradation temperature on the activity of the RuO_2/γ-Al_2O_3 catalyst were investigated and thereaction mechanism was preliminarily studied. Results showed that uniform dispersion of RuO_2crystallites was observed on the surface of the catalyst. The activity of the catalyst was higher atcalcination temperature of 300℃ for 3 h and the particle reunion occurred and some large RuO_2crystallites were abundant at high calcination temperature of 500℃ The activity of the catalyst wasbetter in the acid solution than in the alkaline solution. Increasing degradation temperature andusing the catalyst could shorten the induction periods so that the phenol and COD removal wereincreased. For RuO_2/γ-Al_2O_3 catalyst, the phenol and COD removal were respectively 98% and 80%in a temperature of 150℃, pH of 5.6 and pressure of 3 MPa after a 2 h reaction. This indicated thatRu/γ-Al_2O_3 catalyst had good activity.