The conversion coating was formed by dipping AA6061 in a fluorotitanate/zirconate acid and amino trimethylene phosphonic acid （ATMP） solution at room temperature. The formation process and the anti-corrosion perform...The conversion coating was formed by dipping AA6061 in a fluorotitanate/zirconate acid and amino trimethylene phosphonic acid （ATMP） solution at room temperature. The formation process and the anti-corrosion performance of the conversion coating were investigated using electrochemical test and salt spray test （SST）, respectively. The electrochemical test shows that the Zr/Ti and ATMP coating improves the corrosion resistance of AA6061 as good as the chromate （VI） coating. But the results of SST show that the corrosion resistance of Zr/Ti and ATMP coating is not as good as the chromate （VI） coating. The corrosion area is less than 2% after 72 h.展开更多
The corrosion behavior of hot dip galvanized steel pretrvated with bis-[triethoxysilylpropyl] tetrasulfide （BTESPT） modified with alumina particles was studied. The corrosion resistance of the passiving films was ev...The corrosion behavior of hot dip galvanized steel pretrvated with bis-[triethoxysilylpropyl] tetrasulfide （BTESPT） modified with alumina particles was studied. The corrosion resistance of the passiving films was evaluated by Tafel polarization curve and electrochemical impedance spectroscopy. The films formed on the galvanized steel substrate were characterized by Fourier transform infrared spectroscopy and energy dispersive X-ray spectrometry. The surface morphology of the treated hot dip galvanized steel samples was observed by Field Emission Scanning Electron Microscope. The results show that the pretrvatments on the basis of silane films modified with nanoalumina particles have reduced both anodic and cathodic current densities, and increased total impedance in the measured frequency, consequently, improving corrosion protection for hot dip galvanized steel during immersion in NaCl solutions compared to chromate films and silane films.展开更多
The amino-tri-（methylenephosphonic acid） layers were adsorbed on the surface of AA6061 aluminum alloy for improving the lacquer adhesion and corrosion inhibition as a substitute for chromate coatings. The surface st...The amino-tri-（methylenephosphonic acid） layers were adsorbed on the surface of AA6061 aluminum alloy for improving the lacquer adhesion and corrosion inhibition as a substitute for chromate coatings. The surface structure and characteristic of the amino-tri-（methylenephosphonic acid） layers on AA6061 aluminum alloy were investigated by means of XPS and ATR-FTIR analysis. The analyzed results showed that the amino-tri-（methylenephosphonic acid） adsorption layers adsorb on the surface of aluminium alloy via acid-base interaction in a bi-dentate conformation. After the amino-tri-（methylenephosphonic acid） layers were coated with epoxy resin, the layers showed good adhesive strength and favorable corrosion resistance in contrast to chromate coatings.展开更多
基金supported by the Science and Technology Plan Project of Liaoning Province,China(No.2006221011).
文摘The conversion coating was formed by dipping AA6061 in a fluorotitanate/zirconate acid and amino trimethylene phosphonic acid （ATMP） solution at room temperature. The formation process and the anti-corrosion performance of the conversion coating were investigated using electrochemical test and salt spray test （SST）, respectively. The electrochemical test shows that the Zr/Ti and ATMP coating improves the corrosion resistance of AA6061 as good as the chromate （VI） coating. But the results of SST show that the corrosion resistance of Zr/Ti and ATMP coating is not as good as the chromate （VI） coating. The corrosion area is less than 2% after 72 h.
基金the National Natural Science Foundation of China(No.50674022).
文摘The corrosion behavior of hot dip galvanized steel pretrvated with bis-[triethoxysilylpropyl] tetrasulfide （BTESPT） modified with alumina particles was studied. The corrosion resistance of the passiving films was evaluated by Tafel polarization curve and electrochemical impedance spectroscopy. The films formed on the galvanized steel substrate were characterized by Fourier transform infrared spectroscopy and energy dispersive X-ray spectrometry. The surface morphology of the treated hot dip galvanized steel samples was observed by Field Emission Scanning Electron Microscope. The results show that the pretrvatments on the basis of silane films modified with nanoalumina particles have reduced both anodic and cathodic current densities, and increased total impedance in the measured frequency, consequently, improving corrosion protection for hot dip galvanized steel during immersion in NaCl solutions compared to chromate films and silane films.
基金the Science and Technology Plan Project of LiaoningProvince, China (No.2006221011)
文摘The amino-tri-（methylenephosphonic acid） layers were adsorbed on the surface of AA6061 aluminum alloy for improving the lacquer adhesion and corrosion inhibition as a substitute for chromate coatings. The surface structure and characteristic of the amino-tri-（methylenephosphonic acid） layers on AA6061 aluminum alloy were investigated by means of XPS and ATR-FTIR analysis. The analyzed results showed that the amino-tri-（methylenephosphonic acid） adsorption layers adsorb on the surface of aluminium alloy via acid-base interaction in a bi-dentate conformation. After the amino-tri-（methylenephosphonic acid） layers were coated with epoxy resin, the layers showed good adhesive strength and favorable corrosion resistance in contrast to chromate coatings.