In order to obtain homogenous Zn-Bi hyper-monotectic alloys and investigate what mechanism the magnetic field functions,we carried out the solidification experiments of Zn-4wt%Bi,5wt%Bi,6wt%Bi,7wt%Bi, 15wt%Bi and 30wt...In order to obtain homogenous Zn-Bi hyper-monotectic alloys and investigate what mechanism the magnetic field functions,we carried out the solidification experiments of Zn-4wt%Bi,5wt%Bi,6wt%Bi,7wt%Bi, 15wt%Bi and 30wt%Bi alloys under a 18T static magnetic field which was set up in LNCMI.Water quenching was also chosen to further damp the segregation caused by Stokes convection and Marangoni movement.The results indicated that when the content of Bismuth is 5-7wt%,the superimposition of 18Tesla magnetic field can damp the segregation remarkably,and the size of the second phase particles also is decreased.Furthermore,to Zn-4wt%Bi alloy solidified in 18T magnetic field,no spherical bismuth particles are found even magnifying 1000 times by microscope, which hints that the 18T magnetic field may change its solidifying character.To Zn-15wt%Bi and Zn-30wt%Bi alloy, due to their strong segregation trend,the 18T magnetic field still cannot damp the Stokes settlement thoroughly even by quenching way,however,no layered bismuth and zinc appears when compared to 0T,large Bismuth block are formed in the lower half part of the sample.展开更多
基金Item Sponsored by National Science Foundation of China (No.50974085No.51034010) +5 种基金Development Foundation for Talents in Shanghai (No.2009046) National High-tech R&D Program of China (No.2009AA03Z109) Key Research and Innovation Program from Shanghai Municipal Education Commission (No.09zz98) Key Project from Science and Technology Commission of Shanghai Municipality (No:09dz120640109dz1206402) EuroMagNET under the EU contract n 228043
文摘In order to obtain homogenous Zn-Bi hyper-monotectic alloys and investigate what mechanism the magnetic field functions,we carried out the solidification experiments of Zn-4wt%Bi,5wt%Bi,6wt%Bi,7wt%Bi, 15wt%Bi and 30wt%Bi alloys under a 18T static magnetic field which was set up in LNCMI.Water quenching was also chosen to further damp the segregation caused by Stokes convection and Marangoni movement.The results indicated that when the content of Bismuth is 5-7wt%,the superimposition of 18Tesla magnetic field can damp the segregation remarkably,and the size of the second phase particles also is decreased.Furthermore,to Zn-4wt%Bi alloy solidified in 18T magnetic field,no spherical bismuth particles are found even magnifying 1000 times by microscope, which hints that the 18T magnetic field may change its solidifying character.To Zn-15wt%Bi and Zn-30wt%Bi alloy, due to their strong segregation trend,the 18T magnetic field still cannot damp the Stokes settlement thoroughly even by quenching way,however,no layered bismuth and zinc appears when compared to 0T,large Bismuth block are formed in the lower half part of the sample.