This study presents an easily prepared film based on alkaline starch-polyvinyl alcohol hybrid and lignin fiber as an additive(SPL film).The SPL film was prepared under acidic conditions through a polycondensation reac...This study presents an easily prepared film based on alkaline starch-polyvinyl alcohol hybrid and lignin fiber as an additive(SPL film).The SPL film was prepared under acidic conditions through a polycondensation reaction of PVA and a mixture incorporating alkaline starch and lignin fiber from agriculture or forest source.The examination using scanning electron microscopy(SEM)showed that the surface of SPL film was smooth and the lignin fiber had good compatibility within the film hybrid.Electrospray ionization mass spectroscopy(ESI-MS)and fourier transform infrared(FTIR)investigations indicated that alkaline starch and lignin fiber reacted with PVA under acidic conditions and that–CH_(2)–O–groups were involved in the cross-linking of the SPL system.In addition,the SPL film exhibited only 4%light transmittance,which effectively reduces the ultraviolet and visible light(UV-Vis)penetration,along with good performance when exposed to thermal degradation,in which the mass loss reached around 60%at 400℃.More-over,the SPL film acquired excellent tensile strength,which is much higher than that of PVA-lignin(PL)composite film.展开更多
基金supported by the Yunnan Provincial Natural Science Foundation(Grant No.202101AT070038)Yunnan Agricultural Joint Fund(202101BD070001-105)+1 种基金China Scholarship Council,and,as well as the Yunnan Provincial Youth Top Talent Project(Grant No.YNWR-QNBJ-2020-166)and Middle-Age Reserve Talents of Academic and Technical Leaders(2019HB026)the 111 Project(D21027).The authors would like to thank Bo-Chen and Shudi-Ren from Shiyanjia Lab(www.shiyanjia.com)for the partly measurements.
文摘This study presents an easily prepared film based on alkaline starch-polyvinyl alcohol hybrid and lignin fiber as an additive(SPL film).The SPL film was prepared under acidic conditions through a polycondensation reaction of PVA and a mixture incorporating alkaline starch and lignin fiber from agriculture or forest source.The examination using scanning electron microscopy(SEM)showed that the surface of SPL film was smooth and the lignin fiber had good compatibility within the film hybrid.Electrospray ionization mass spectroscopy(ESI-MS)and fourier transform infrared(FTIR)investigations indicated that alkaline starch and lignin fiber reacted with PVA under acidic conditions and that–CH_(2)–O–groups were involved in the cross-linking of the SPL system.In addition,the SPL film exhibited only 4%light transmittance,which effectively reduces the ultraviolet and visible light(UV-Vis)penetration,along with good performance when exposed to thermal degradation,in which the mass loss reached around 60%at 400℃.More-over,the SPL film acquired excellent tensile strength,which is much higher than that of PVA-lignin(PL)composite film.