BiOI-sensitized titanium dioxide (TiO2) photocatalysts were prepared by a deposition method at room temperature and characterized by X-ray diffraction, X-ray photoelectron spectroscopy, and Brunauer–Emmett–Teller su...BiOI-sensitized titanium dioxide (TiO2) photocatalysts were prepared by a deposition method at room temperature and characterized by X-ray diffraction, X-ray photoelectron spectroscopy, and Brunauer–Emmett–Teller surface area measurements. The photocatalytic activities of the catalysts were evaluated for the degradation of methyl orange (MO) solution under UV and visible light irradiation. The effects of catalyst amount, initial pH value, initial concentration of MO, as well as KI amount were investigated. The repeatability of photocatalytic activity of the 1.7% BiOI/TiO2 catalyst was also tested. It is shown that BiOI sensitization enhances the photocatalytic activities of TiO2. With BiOI content increasing, the photocatalytic activities of BiOI/TiO2 under UV and visible light irradiation first increase, reaching a maximum around BiOI content of 1.7%, and then decrease with further increasing BiOI content. The 1.7% BiOI/TiO2 catalyst obviously exhibits much higher visible light photocatalytic activity than P25, and its UV light photocatalytic activity is slightly higher than that of P25. Under the conditions of a catalytic dose of 1.5 g.L-1, initial pH of 3.0, initial MO concentration of 20 mg.L-1, UV power of 300 W, and air flow rate of 0.8 L.min-1, complete degradatio is achieved within 60 min. The repeatability of photocatalytic activity of the 1.7% BiOI/TiO2 catalyst is highly reliable.展开更多
Complex nanometer particles WO3/TiO2 were prepared using a sol-gel process and characterized using XRD spectra. The photocatalytic activity of TiO2 can be increased by doping W^6＋ with TiO2 because the doped W^6＋ th...Complex nanometer particles WO3/TiO2 were prepared using a sol-gel process and characterized using XRD spectra. The photocatalytic activity of TiO2 can be increased by doping W^6＋ with TiO2 because the doped W^6＋ that entered into the crystal lattices of TiO2 led to the formation of defects in the crystal lattices of TiO2 and thereby improved the photocatalytic activity of TiO2.When WO3 doped in TiO2 exceeded 3%, the excess W^6＋ did not enter into the crystal lattices of TiO2 but were uniformly dispersed in TiO2 or they covered the surface of TiO2, which reduced the effective illumination area of TiO2 and thereby lowered the photocatalytic activity of TiOE.The relationship among the composition of the catalyst, the amount of photocatalyst, the illumination time, and the decolorizing rate of methyl orange （MO） were discussed. The results show that the decolorizing rate of MO can reach 82.3% using WO3/TiO2 as the photocatalyst, with the composition of WO3/TiO2 -3：97, the mass of catalyst = 0.400 g, the initial concentration of MO = 20 mg/L, pH = 6.5, and the illumina- tion time = 7 h.展开更多
基金financially supported by the National Natural Science Foundation of China(No.21171091)the Natural Science Foundation of Higher Education Institutions in Anhui Province(Nos.KJ2012A217,KJ2012B135,and KJ2012B136)
文摘BiOI-sensitized titanium dioxide (TiO2) photocatalysts were prepared by a deposition method at room temperature and characterized by X-ray diffraction, X-ray photoelectron spectroscopy, and Brunauer–Emmett–Teller surface area measurements. The photocatalytic activities of the catalysts were evaluated for the degradation of methyl orange (MO) solution under UV and visible light irradiation. The effects of catalyst amount, initial pH value, initial concentration of MO, as well as KI amount were investigated. The repeatability of photocatalytic activity of the 1.7% BiOI/TiO2 catalyst was also tested. It is shown that BiOI sensitization enhances the photocatalytic activities of TiO2. With BiOI content increasing, the photocatalytic activities of BiOI/TiO2 under UV and visible light irradiation first increase, reaching a maximum around BiOI content of 1.7%, and then decrease with further increasing BiOI content. The 1.7% BiOI/TiO2 catalyst obviously exhibits much higher visible light photocatalytic activity than P25, and its UV light photocatalytic activity is slightly higher than that of P25. Under the conditions of a catalytic dose of 1.5 g.L-1, initial pH of 3.0, initial MO concentration of 20 mg.L-1, UV power of 300 W, and air flow rate of 0.8 L.min-1, complete degradatio is achieved within 60 min. The repeatability of photocatalytic activity of the 1.7% BiOI/TiO2 catalyst is highly reliable.
基金This work was financially supported by the Natural Science Foundation of Anhui Province, China (No. 050450301).
文摘Complex nanometer particles WO3/TiO2 were prepared using a sol-gel process and characterized using XRD spectra. The photocatalytic activity of TiO2 can be increased by doping W^6＋ with TiO2 because the doped W^6＋ that entered into the crystal lattices of TiO2 led to the formation of defects in the crystal lattices of TiO2 and thereby improved the photocatalytic activity of TiO2.When WO3 doped in TiO2 exceeded 3%, the excess W^6＋ did not enter into the crystal lattices of TiO2 but were uniformly dispersed in TiO2 or they covered the surface of TiO2, which reduced the effective illumination area of TiO2 and thereby lowered the photocatalytic activity of TiOE.The relationship among the composition of the catalyst, the amount of photocatalyst, the illumination time, and the decolorizing rate of methyl orange （MO） were discussed. The results show that the decolorizing rate of MO can reach 82.3% using WO3/TiO2 as the photocatalyst, with the composition of WO3/TiO2 -3：97, the mass of catalyst = 0.400 g, the initial concentration of MO = 20 mg/L, pH = 6.5, and the illumina- tion time = 7 h.