The overall decarburization mechanism can be divided into the decarburization in bulk molten steel and floating of CO against static pressure, the decarburization on the surface of argon bubbles and splashing particle...The overall decarburization mechanism can be divided into the decarburization in bulk molten steel and floating of CO against static pressure, the decarburization on the surface of argon bubbles and splashing particles. On the basis of each conception the RH-MFB decarburization mathematical model has been built according to the thermodynamic and mass conservation principle, and contributions of every decarburization mechanism were discussed and analyzed.展开更多
Using 0.6-scale warer modelling based on Fr-We number similitude criteria, the influences of the submerged entry nozzle configuration and operating practices on the level fluctuation in the mold which caused surface d...Using 0.6-scale warer modelling based on Fr-We number similitude criteria, the influences of the submerged entry nozzle configuration and operating practices on the level fluctuation in the mold which caused surface defects and mold power catching, were studied. It was found that the level flunction was resulted from gas injection, impacting of the stream and standing wave. The level turblence raises with the incresing of the gas injection, however the casting rate, immersion depth and jet angel of SEN have a dual influenc on the level fluctuation.展开更多
文摘The overall decarburization mechanism can be divided into the decarburization in bulk molten steel and floating of CO against static pressure, the decarburization on the surface of argon bubbles and splashing particles. On the basis of each conception the RH-MFB decarburization mathematical model has been built according to the thermodynamic and mass conservation principle, and contributions of every decarburization mechanism were discussed and analyzed.
文摘Using 0.6-scale warer modelling based on Fr-We number similitude criteria, the influences of the submerged entry nozzle configuration and operating practices on the level fluctuation in the mold which caused surface defects and mold power catching, were studied. It was found that the level flunction was resulted from gas injection, impacting of the stream and standing wave. The level turblence raises with the incresing of the gas injection, however the casting rate, immersion depth and jet angel of SEN have a dual influenc on the level fluctuation.