Magnetite is a kind of iron ore that is difficult to carburize.In order to improve the carburizing performance of magnetite pellet,pre-oxidation treatment was carried out,and the oxidation,reduction and carburization ...Magnetite is a kind of iron ore that is difficult to carburize.In order to improve the carburizing performance of magnetite pellet,pre-oxidation treatment was carried out,and the oxidation,reduction and carburization behaviors of magnetite pellet were investigated in this study.The magnetite pellet was oxidized in the air and carburized in CO-CO_(2)-H_(2) gas mixtures,the oxidation,reduction and carburization behaviors were demonstrated by detecting phase change,microstructure,carburizing index via thermogravimetry,X-ray diffraction(XRD),infrared carbon-sulfur analyzer,and scanning electron microscope(SEM).The results show that the dense magnetite particles inside pellet are oxidized to porous hematite particles,and the Fe_(3)O_(4) transforms to Fe_(2)O_(3) with high lattice defect concentration during the pre-oxidation process.Then the porous hematite particles and newly formed Fe_(2)O_(3) significantly promote the reduction efficiency.Porous metallic iron particles are produced in the reduction process.Finally,both high reduction efficiency and the porous structure of metallic iron particles dramatically enhance the carburization efficiency of pellet.High preoxidation temperature favors to the carburization of magnetite pellet.However,the carburized index decreases due to the recrystallization of iron oxide when the temperature extends to 1000℃.The optimum pre-oxidation temperature for magnetite pellet carburization is 900℃.展开更多
Anodization is a popular method of preparing TiO2nanotube array films（TiNTs） by using direct current（DC）power as the driving voltage.In this study,three driving voltage modes,namely,the sine alternating current（s...Anodization is a popular method of preparing TiO2nanotube array films（TiNTs） by using direct current（DC）power as the driving voltage.In this study,three driving voltage modes,namely,the sine alternating current（sine） mode,the full-wave rectification of sine waves via four diodes（sine-4D,where D means diode） mode,and the DC mode,were used to prepare TiNTs by anodization.At 20 V,TiNTs were formed under sine-4D mode but only irregular porous TiO2films were formed under DC mode.At 50 V,TiNTs formed under both the sine-4D and DC modes.No TiNTs formed in the sine mode anodization at either 20 or 50 V.Compared with the DC mode,the sine-4D mode required a lower oxidation voltage for TiNT formation,which suggests that sine-4D is an economical,convenient,and efficient driving voltage for TiNT preparation by anodization.The morphologies and structures of TiNT samples anodized at 50 V in the sine-4D and DC modes at different oxidation time（1,5,10,30,60,and 120 min） were analyzed.TiNT growth processes were similar between the studied modes.However,the growth rate of the films was faster under the sine-4D mode than the DC mode during the first 30 min of anodization.展开更多
基金Project supported by the National Natural Science Foundation of China(No.21502076)the Hundred-Talent Program of Hefei Citythe Outstanding Young Talents Scheme of Jiangxi Province(No.20171BCB23039)~~
基金Project(U1960104)supported by the National Natural Science Foundation of ChinaProject(LYU Ya-nan)supported by the Jiangsu Colleges and Universities Qing Lan Project,China。
文摘Magnetite is a kind of iron ore that is difficult to carburize.In order to improve the carburizing performance of magnetite pellet,pre-oxidation treatment was carried out,and the oxidation,reduction and carburization behaviors of magnetite pellet were investigated in this study.The magnetite pellet was oxidized in the air and carburized in CO-CO_(2)-H_(2) gas mixtures,the oxidation,reduction and carburization behaviors were demonstrated by detecting phase change,microstructure,carburizing index via thermogravimetry,X-ray diffraction(XRD),infrared carbon-sulfur analyzer,and scanning electron microscope(SEM).The results show that the dense magnetite particles inside pellet are oxidized to porous hematite particles,and the Fe_(3)O_(4) transforms to Fe_(2)O_(3) with high lattice defect concentration during the pre-oxidation process.Then the porous hematite particles and newly formed Fe_(2)O_(3) significantly promote the reduction efficiency.Porous metallic iron particles are produced in the reduction process.Finally,both high reduction efficiency and the porous structure of metallic iron particles dramatically enhance the carburization efficiency of pellet.High preoxidation temperature favors to the carburization of magnetite pellet.However,the carburized index decreases due to the recrystallization of iron oxide when the temperature extends to 1000℃.The optimum pre-oxidation temperature for magnetite pellet carburization is 900℃.
基金the financial support provided by the National Natural Science Foundation of China (Nos. 21277004, 21190051 and 41121004)the Beijing Natural Science Foundation, China (No. 8132035)
文摘Anodization is a popular method of preparing TiO2nanotube array films（TiNTs） by using direct current（DC）power as the driving voltage.In this study,three driving voltage modes,namely,the sine alternating current（sine） mode,the full-wave rectification of sine waves via four diodes（sine-4D,where D means diode） mode,and the DC mode,were used to prepare TiNTs by anodization.At 20 V,TiNTs were formed under sine-4D mode but only irregular porous TiO2films were formed under DC mode.At 50 V,TiNTs formed under both the sine-4D and DC modes.No TiNTs formed in the sine mode anodization at either 20 or 50 V.Compared with the DC mode,the sine-4D mode required a lower oxidation voltage for TiNT formation,which suggests that sine-4D is an economical,convenient,and efficient driving voltage for TiNT preparation by anodization.The morphologies and structures of TiNT samples anodized at 50 V in the sine-4D and DC modes at different oxidation time（1,5,10,30,60,and 120 min） were analyzed.TiNT growth processes were similar between the studied modes.However,the growth rate of the films was faster under the sine-4D mode than the DC mode during the first 30 min of anodization.