To investigate the effects of extrusion temperature on the microstructure and mechanical properties of WE43 magnesium alloy,extrusion experiments were conducted under 330,380,430,and 450℃,and the extrusion ratio was ...To investigate the effects of extrusion temperature on the microstructure and mechanical properties of WE43 magnesium alloy,extrusion experiments were conducted under 330,380,430,and 450℃,and the extrusion ratio was 16.The experimental results indicate that,at a low temperature of 330℃,the alloy precipitates a large amount of second phases rich in Zr elements.Moreover,the texture strength and kernel average misorientation value are the highest,with values of 27.77 and 0.71,respectively.The increase in extrusion temperature leads to a gradual decrease in texture strength and kernel average misorientation value.The strength of the alloy is the highest at an extrusion temperature of 330℃.Its tensile yield stress is 254.7 MPa and ultimate tensile strength is 302.7 MPa,respectively.As the extrusion temperature increases,the strength of the alloy gradually decreases.At an extrusion temperature of 450℃,the tensile yield stress is 181.3 MPa and ultimate tensile strength is 265.7 MPa,respectively.The elongation first increases and then decreases,with an elongation of 20.9%at an extrusion temperature of 330℃.At an extrusion temperature of 430℃,the elongation reaches its maximum value,which is 23.6%.At an extrusion temperature of 450℃,the elongation reaches its lowest value,which is 16.4%.展开更多
Self-designed Al8Si0.4Mg0.4Fe aluminium alloy was modified with Sr,followed by solid solution and aging treatments to regulate its microstructure and mechanical/electrical properties.The results show that after the mo...Self-designed Al8Si0.4Mg0.4Fe aluminium alloy was modified with Sr,followed by solid solution and aging treatments to regulate its microstructure and mechanical/electrical properties.The results show that after the modification treatment,the room-temperature tensile strength of the alloy remains nearly unchanged,the elongation at break slightly increases from 1.82%to 3.34%,and the electrical conductivity significantly increases from 40.1%international annealed copper standard(IACS)to 42.0%IACS.After the modification,the alloy was subjected to solid solution treatment at 515℃for 8 h,followed by aging treatment at 180,200,220 and 240℃for 6 h.With increasing aging temperature,the electrical conductivity increases monotonously from 41.4%IACS to 45.5%IACS,while the room-temperature tensile strength initially increases and then decreases.At 200℃,the alloy achieves an optimal balance between electrical conductivity and room-temperature tensile strength:the electrical conductivity is 42.5%IACS,and the room-temperature tensile strength is 282.9 MPa.When the aging temperature continues to rise,the alloy undergoes overaging.Although the conductivity continues to increase,the room-temperature tensile strength drops sharply,and it is only 177.1 MPa at 240℃.展开更多
基金Funded by the Fundamental Research Program of Shanxi Province(No.202203021211191)。
文摘To investigate the effects of extrusion temperature on the microstructure and mechanical properties of WE43 magnesium alloy,extrusion experiments were conducted under 330,380,430,and 450℃,and the extrusion ratio was 16.The experimental results indicate that,at a low temperature of 330℃,the alloy precipitates a large amount of second phases rich in Zr elements.Moreover,the texture strength and kernel average misorientation value are the highest,with values of 27.77 and 0.71,respectively.The increase in extrusion temperature leads to a gradual decrease in texture strength and kernel average misorientation value.The strength of the alloy is the highest at an extrusion temperature of 330℃.Its tensile yield stress is 254.7 MPa and ultimate tensile strength is 302.7 MPa,respectively.As the extrusion temperature increases,the strength of the alloy gradually decreases.At an extrusion temperature of 450℃,the tensile yield stress is 181.3 MPa and ultimate tensile strength is 265.7 MPa,respectively.The elongation first increases and then decreases,with an elongation of 20.9%at an extrusion temperature of 330℃.At an extrusion temperature of 430℃,the elongation reaches its maximum value,which is 23.6%.At an extrusion temperature of 450℃,the elongation reaches its lowest value,which is 16.4%.
基金Applied Basic Research Program of Liaoning Province(CN)(2022JH2/101300078)。
文摘Self-designed Al8Si0.4Mg0.4Fe aluminium alloy was modified with Sr,followed by solid solution and aging treatments to regulate its microstructure and mechanical/electrical properties.The results show that after the modification treatment,the room-temperature tensile strength of the alloy remains nearly unchanged,the elongation at break slightly increases from 1.82%to 3.34%,and the electrical conductivity significantly increases from 40.1%international annealed copper standard(IACS)to 42.0%IACS.After the modification,the alloy was subjected to solid solution treatment at 515℃for 8 h,followed by aging treatment at 180,200,220 and 240℃for 6 h.With increasing aging temperature,the electrical conductivity increases monotonously from 41.4%IACS to 45.5%IACS,while the room-temperature tensile strength initially increases and then decreases.At 200℃,the alloy achieves an optimal balance between electrical conductivity and room-temperature tensile strength:the electrical conductivity is 42.5%IACS,and the room-temperature tensile strength is 282.9 MPa.When the aging temperature continues to rise,the alloy undergoes overaging.Although the conductivity continues to increase,the room-temperature tensile strength drops sharply,and it is only 177.1 MPa at 240℃.