Ceramic slurry of 78 mass%solid loading was prepared using photosensitive acrylic resin and dispersant SP-710 as the liquid phase,Al_(2)O_(3) powder(d50=2.38μm)and TiO_(2) powder additive as the solid phase.Alumina c...Ceramic slurry of 78 mass%solid loading was prepared using photosensitive acrylic resin and dispersant SP-710 as the liquid phase,Al_(2)O_(3) powder(d50=2.38μm)and TiO_(2) powder additive as the solid phase.Alumina ceramics were prepared by DLP,sintering for 4 h at 1450,1500,1550 or 1600℃,respectively.The effects of the TiO_(2) addition(0,1%,2%,3%and 5%,by mass)on the properties of the ceramics were studied.The results show that the addition of TiO_(2) can improve the sintering of Al_(2)O_(3) ceramics,significantly improve the densification,and reduce the sintering temperature.With the optimum TiO_(2) addition of 3%and the optimum sintering temperature of 1600℃,the obtained Al_(2)O_(3) ceramics have shrinkage of 15.7%,15.8%and 23.8%at the x axis,the y axis,and the z axis,respectively,the porosity of 2.4%,the bulk density of 3.74 g·cm-3 and the three-point bending strength of 251.1 MPa.Compared with the undoped alumina ceramics,the doped alumina ceramic has increased bulk density by 0.56 g·cm-3,decreased apparent porosity from 20.2%to 2.4%,and the three-point bending strength increases by 2.5 times.Therefore,the density and the strength of DLP prepared ceramics can be improved effectively by adding an appropriate amount of TiO_(2),and the performance of the DLP prepared ceramics is close to that of the pressed samples.Thus,it is hopeful to apply DLP in refractories field.展开更多
文摘Ceramic slurry of 78 mass%solid loading was prepared using photosensitive acrylic resin and dispersant SP-710 as the liquid phase,Al_(2)O_(3) powder(d50=2.38μm)and TiO_(2) powder additive as the solid phase.Alumina ceramics were prepared by DLP,sintering for 4 h at 1450,1500,1550 or 1600℃,respectively.The effects of the TiO_(2) addition(0,1%,2%,3%and 5%,by mass)on the properties of the ceramics were studied.The results show that the addition of TiO_(2) can improve the sintering of Al_(2)O_(3) ceramics,significantly improve the densification,and reduce the sintering temperature.With the optimum TiO_(2) addition of 3%and the optimum sintering temperature of 1600℃,the obtained Al_(2)O_(3) ceramics have shrinkage of 15.7%,15.8%and 23.8%at the x axis,the y axis,and the z axis,respectively,the porosity of 2.4%,the bulk density of 3.74 g·cm-3 and the three-point bending strength of 251.1 MPa.Compared with the undoped alumina ceramics,the doped alumina ceramic has increased bulk density by 0.56 g·cm-3,decreased apparent porosity from 20.2%to 2.4%,and the three-point bending strength increases by 2.5 times.Therefore,the density and the strength of DLP prepared ceramics can be improved effectively by adding an appropriate amount of TiO_(2),and the performance of the DLP prepared ceramics is close to that of the pressed samples.Thus,it is hopeful to apply DLP in refractories field.