In order to prepare high density magnesium aluminate spinel materials,the light-burned magnesia and alumina powder were used as the main raw materials.Active magnesium aluminate spinel powders were synthesized at diff...In order to prepare high density magnesium aluminate spinel materials,the light-burned magnesia and alumina powder were used as the main raw materials.Active magnesium aluminate spinel powders were synthesized at different temperatures,and the sintering properties of the synthesized materials were characterized.The results show that the optimal light-burned temperature for synthesizing active magnesium aluminate spinel raw materials with small grain sizes and high sintering activity is 1400℃.The active spinel raw materials were sintered at 1750℃ for 3 h to form a dense spinel material,in which the spinel grains were well developed,exhibited a dense interlocking structure,and were uniformly distributed,with an average grain size of about 7.26μm.The bulk density and apparent porosity of the dense spinel material were 3.29 g·cm^(-3) and 3.5%,respectively.展开更多
文摘In order to prepare high density magnesium aluminate spinel materials,the light-burned magnesia and alumina powder were used as the main raw materials.Active magnesium aluminate spinel powders were synthesized at different temperatures,and the sintering properties of the synthesized materials were characterized.The results show that the optimal light-burned temperature for synthesizing active magnesium aluminate spinel raw materials with small grain sizes and high sintering activity is 1400℃.The active spinel raw materials were sintered at 1750℃ for 3 h to form a dense spinel material,in which the spinel grains were well developed,exhibited a dense interlocking structure,and were uniformly distributed,with an average grain size of about 7.26μm.The bulk density and apparent porosity of the dense spinel material were 3.29 g·cm^(-3) and 3.5%,respectively.