The effects of an external DC(direct current)electric field on recrystallization texture evolution in the cold-rolled aluminum sheets with 99.99%purity were investigated by means of X-ray diffraction techniques.The co...The effects of an external DC(direct current)electric field on recrystallization texture evolution in the cold-rolled aluminum sheets with 99.99%purity were investigated by means of X-ray diffraction techniques.The cold-rolled high-purity aluminum sheets were annealed for 60 min at 200,300 and 400℃,respectively with and without an external DC electric field of 800 V/mm.The results show that with DC electric field,the recrystallization cube texture is strengthened at the stage of grain growth. Possible reason for the strengthening of the recrystallization cube texture with the applied electric field may be attributed to both selected nucleation and selected growth of cube oriented crystal nuclei.展开更多
The commercially pure copper with dimension of 80 mm×20 mm×4 mm was used for equal channel angular pressing (ECAP), of which their outward appearance coordinate is corresponded with that of rolling deformati...The commercially pure copper with dimension of 80 mm×20 mm×4 mm was used for equal channel angular pressing (ECAP), of which their outward appearance coordinate is corresponded with that of rolling deformation modes. Cold-deformed texture was investigated. The results show that the texture character in pure copper processed by ECAP is related with intersection angle (Φ) of the die channel. When Φ is 90° and the sample is extruded for one pass, its texture consists of α and β orientation lines including mainly C, B, S and Goss components, moreover a little rotated cube is found. When Φ is 135°, as extrusion pass increases, the weak texture forms on the scope of deviation from rotated cube (ψ=0°, θ=0°,φ=450°±150°) and develops to the ψ=45° fiber mainly including rotated cube. When Φ is 120°, the texture is ψ=45° fiber mainly including rotated cube that is maintained constant as extrusion pass increases.展开更多
基金Project(50374028)supported by the National Natural Science Foundation of China and Shanghai Bao Steel Group of ChinaProject(PRAMX04-02)supported by Sino-French Cooperation Program
文摘The effects of an external DC(direct current)electric field on recrystallization texture evolution in the cold-rolled aluminum sheets with 99.99%purity were investigated by means of X-ray diffraction techniques.The cold-rolled high-purity aluminum sheets were annealed for 60 min at 200,300 and 400℃,respectively with and without an external DC electric field of 800 V/mm.The results show that with DC electric field,the recrystallization cube texture is strengthened at the stage of grain growth. Possible reason for the strengthening of the recrystallization cube texture with the applied electric field may be attributed to both selected nucleation and selected growth of cube oriented crystal nuclei.
基金Project(Lnzr0201) supported by the Foundation of Science and Technology Committee of Liaoning Province of China
文摘The commercially pure copper with dimension of 80 mm×20 mm×4 mm was used for equal channel angular pressing (ECAP), of which their outward appearance coordinate is corresponded with that of rolling deformation modes. Cold-deformed texture was investigated. The results show that the texture character in pure copper processed by ECAP is related with intersection angle (Φ) of the die channel. When Φ is 90° and the sample is extruded for one pass, its texture consists of α and β orientation lines including mainly C, B, S and Goss components, moreover a little rotated cube is found. When Φ is 135°, as extrusion pass increases, the weak texture forms on the scope of deviation from rotated cube (ψ=0°, θ=0°,φ=450°±150°) and develops to the ψ=45° fiber mainly including rotated cube. When Φ is 120°, the texture is ψ=45° fiber mainly including rotated cube that is maintained constant as extrusion pass increases.