<001>textured Pb(Ni_(1/3)Nb_(2/3))O_(3)-PbZrO_(3)-PbTiO_(3)(PNN-PZT)ceramics were prepared by templated grain growth(TGG)technique using 0.36PNN-x PZ-(0.64-x)PT(x=0.23,0.25 and 0.27)powder matrix.Optimum templat...<001>textured Pb(Ni_(1/3)Nb_(2/3))O_(3)-PbZrO_(3)-PbTiO_(3)(PNN-PZT)ceramics were prepared by templated grain growth(TGG)technique using 0.36PNN-x PZ-(0.64-x)PT(x=0.23,0.25 and 0.27)powder matrix.Optimum template content was derived to achieve the best electromechanical properties of textured ceramics.The piezoelectric coefficient d33=1165 pC/N,Curie temperature T_(C)=197℃,longitudinal mode electrome-chanical coupling factor k33=0.86 and a very large effective piezoelectric strain coefficient d_(33)^(*)=2041 pm/V were simultaneously achieved at the morphotropic phase boundary(MPB)composition(x=0.25)with 3 vol.%BaTiO_(3)(BT)templates.Domain structures of textured ceramics were analyzed in detail to reveal the origin of these high piezoelectric and electromechanical properties.展开更多
The reaction process and mechanistn of reaction synthesis of TiC in Al-Ti-C system have been investigated in detail by observing the microstructure of the water quenched preform with SEM and EDX. The results showed th...The reaction process and mechanistn of reaction synthesis of TiC in Al-Ti-C system have been investigated in detail by observing the microstructure of the water quenched preform with SEM and EDX. The results showed that the reaction processing can be divided into three stages: aluminium powder is melted firstly, then titanium dissolves in the melted aluminium and Al3Ti is formed around titanium powder, titanium concentrates around carbon powder and a Ti-rich layer is observed around carbon pariicles,in which titanium atom reacts with carbon atom to synthesize TiC;TiC precipitates out of the melt, and diffuses out of the layer. A solution-precipitation mechanism and a reaction model were set up based on the experimental results.展开更多
Potential field due to line sources residing on slender heterogeneities is involved in various areas,such as heat conduction,potential flow,and electrostatics.Often dipolar line sources are either prescribed or induce...Potential field due to line sources residing on slender heterogeneities is involved in various areas,such as heat conduction,potential flow,and electrostatics.Often dipolar line sources are either prescribed or induced due to close interaction with other objects.Its calculation requires a higher-order scheme to take into account the dipolar effect as well as net source effect.In the present work,we apply such a higher-order line element method to analyze the potential field with cylindrical slender heterogeneities.In a benchmark example of two parallel rods,we compare the line element solution with the boundary element solution to show the accuracy as a function in terms of rods distance.Furthermore,we use more complicated examples to demonstrate the capability of the line element technique.展开更多
The crack initiation mechanism of a Z3CN20.09M duplex stainless steel （DSS） during corrosion fatigue （CF） in water and air at 290 ℃ was investigated by using a CF cracking machine and a scanning electron microsco...The crack initiation mechanism of a Z3CN20.09M duplex stainless steel （DSS） during corrosion fatigue （CF） in water and air at 290 ℃ was investigated by using a CF cracking machine and a scanning electron microscopy （SEM）. The cracks were initiated successively at the persistent stip bands （PSBs）, phase boundaries （PBs） and pitting corrosion points （PCPs） of the specimens when they were tested in water at 290 ℃, while in airat 290 ℃ the cracks were only initiated at the PSBs and PBs. And the cracks were found mainly to initiate at the PSBs and PBs when the specimens were tested in water and air at 290 ℃, respectively. The results also reveal that the cracks were likely to be initiated at the first 20% of fatigue life of the specimens tested in water at 290 ℃. However, the cracks were not found until 50% of fatigue life when tested in air at 290 ℃. Moreover, the crack numbers of the specimens tested in water at 290 ℃ were much more than those tested in air at 290 ℃.展开更多
Two low-lying unbound states in ^(16)C are investigated by deuteron inelastic scattering in inverse kinematics.Besides the 2^(-) state at 5.45 MeV previously measured in a 1n knockout reaction,a new resonant state at ...Two low-lying unbound states in ^(16)C are investigated by deuteron inelastic scattering in inverse kinematics.Besides the 2^(-) state at 5.45 MeV previously measured in a 1n knockout reaction,a new resonant state at 6.89 MeV is observed for the first time.The inelastic scattering angular distributions of these two states are well reproduced by the distorted-wave Born approximation(DWBA)calculation with an l=1 excitation.In addition,the spinparities of the unbound states are discussed and tentatively assigned based on shell model calculations using the modified YSOX interaction.展开更多
基金supported in part by the Natural Science Foun-dation of Heilongjiang Province(No.LH2022E048)Postdoctoral Science Foundation of Heilongjiang Province(No.LBH-Z22138)China National Postdoctoral Program for Innovative Talents(No.BX20490103).
文摘<001>textured Pb(Ni_(1/3)Nb_(2/3))O_(3)-PbZrO_(3)-PbTiO_(3)(PNN-PZT)ceramics were prepared by templated grain growth(TGG)technique using 0.36PNN-x PZ-(0.64-x)PT(x=0.23,0.25 and 0.27)powder matrix.Optimum template content was derived to achieve the best electromechanical properties of textured ceramics.The piezoelectric coefficient d33=1165 pC/N,Curie temperature T_(C)=197℃,longitudinal mode electrome-chanical coupling factor k33=0.86 and a very large effective piezoelectric strain coefficient d_(33)^(*)=2041 pm/V were simultaneously achieved at the morphotropic phase boundary(MPB)composition(x=0.25)with 3 vol.%BaTiO_(3)(BT)templates.Domain structures of textured ceramics were analyzed in detail to reveal the origin of these high piezoelectric and electromechanical properties.
文摘The reaction process and mechanistn of reaction synthesis of TiC in Al-Ti-C system have been investigated in detail by observing the microstructure of the water quenched preform with SEM and EDX. The results showed that the reaction processing can be divided into three stages: aluminium powder is melted firstly, then titanium dissolves in the melted aluminium and Al3Ti is formed around titanium powder, titanium concentrates around carbon powder and a Ti-rich layer is observed around carbon pariicles,in which titanium atom reacts with carbon atom to synthesize TiC;TiC precipitates out of the melt, and diffuses out of the layer. A solution-precipitation mechanism and a reaction model were set up based on the experimental results.
文摘Potential field due to line sources residing on slender heterogeneities is involved in various areas,such as heat conduction,potential flow,and electrostatics.Often dipolar line sources are either prescribed or induced due to close interaction with other objects.Its calculation requires a higher-order scheme to take into account the dipolar effect as well as net source effect.In the present work,we apply such a higher-order line element method to analyze the potential field with cylindrical slender heterogeneities.In a benchmark example of two parallel rods,we compare the line element solution with the boundary element solution to show the accuracy as a function in terms of rods distance.Furthermore,we use more complicated examples to demonstrate the capability of the line element technique.
基金financial support from the"863"Program of China under Nos.2008AA031702 and 2012AA03A507
文摘The crack initiation mechanism of a Z3CN20.09M duplex stainless steel （DSS） during corrosion fatigue （CF） in water and air at 290 ℃ was investigated by using a CF cracking machine and a scanning electron microscopy （SEM）. The cracks were initiated successively at the persistent stip bands （PSBs）, phase boundaries （PBs） and pitting corrosion points （PCPs） of the specimens when they were tested in water at 290 ℃, while in airat 290 ℃ the cracks were only initiated at the PSBs and PBs. And the cracks were found mainly to initiate at the PSBs and PBs when the specimens were tested in water and air at 290 ℃, respectively. The results also reveal that the cracks were likely to be initiated at the first 20% of fatigue life of the specimens tested in water at 290 ℃. However, the cracks were not found until 50% of fatigue life when tested in air at 290 ℃. Moreover, the crack numbers of the specimens tested in water at 290 ℃ were much more than those tested in air at 290 ℃.
基金Supported by the National Key R&D Program of China(2018YFA0404403)the National Natural Science Foundation of China(11775004,U1867214,11875074,11961141003)+1 种基金the funding from the State Key Laboratory of Nuclear Physics and Technology,Peking University(NPT2021ZZ01)the funding from Heavy Ion Research Facility in Lanzhou(HIR2021PY002)。
文摘Two low-lying unbound states in ^(16)C are investigated by deuteron inelastic scattering in inverse kinematics.Besides the 2^(-) state at 5.45 MeV previously measured in a 1n knockout reaction,a new resonant state at 6.89 MeV is observed for the first time.The inelastic scattering angular distributions of these two states are well reproduced by the distorted-wave Born approximation(DWBA)calculation with an l=1 excitation.In addition,the spinparities of the unbound states are discussed and tentatively assigned based on shell model calculations using the modified YSOX interaction.