A Pb-0.08Ca-2Sn alloy was subjected to rolling at room temperature to different final thicknesses.Annealing treatments at temperature ranging from 80 to 120 °C led to recrystallization of the samples as shown by ...A Pb-0.08Ca-2Sn alloy was subjected to rolling at room temperature to different final thicknesses.Annealing treatments at temperature ranging from 80 to 120 °C led to recrystallization of the samples as shown by resistivity and micro-hardness measurements.The deformation texture determined through X-ray diffraction is qualitatively the Brass type.The measured Lankford anisotropy parameter R and its evolution are close to the determined one using a self consistent approach.The R value evolution with angle to rolling direction shows the presence of planar anisotropy and poor drawability.The recrystallization in annealing at 80-120 °C is achieved within time period up to 3×104 s.The recrystallization texture is a retained deformation texture with an emerging Cube component.展开更多
In this work,the micromechanical properties,crystallographic texture,welding residual stresses and their evolution after plastic strain were investigated in a Ti-6Al-4V alloy tungsten inert gas weld joint.It was found...In this work,the micromechanical properties,crystallographic texture,welding residual stresses and their evolution after plastic strain were investigated in a Ti-6Al-4V alloy tungsten inert gas weld joint.It was found that the welding process affected the Young modulus and microhardness values in bothαandβphases in the different regions of the weld joint.The highest microhardness and Young modulus values of a phase were recorded in the heat-affected zone,whereas the highest values of these characteristics for theβphase were found in the fusion zone(FZ).The change in the micro mechanical properties was accompanied by a change in the crystallographic texture components of the dominant a phase from(0001)<10-10>and(11-20)<10-10>components in the base material to(10-10)<11-20>and(11-20)<3-302>components in the FZ.The introduction of tensile testing resulted in a continuous stress relaxation and improved the weld joint performances.展开更多
文摘A Pb-0.08Ca-2Sn alloy was subjected to rolling at room temperature to different final thicknesses.Annealing treatments at temperature ranging from 80 to 120 °C led to recrystallization of the samples as shown by resistivity and micro-hardness measurements.The deformation texture determined through X-ray diffraction is qualitatively the Brass type.The measured Lankford anisotropy parameter R and its evolution are close to the determined one using a self consistent approach.The R value evolution with angle to rolling direction shows the presence of planar anisotropy and poor drawability.The recrystallization in annealing at 80-120 °C is achieved within time period up to 3×104 s.The recrystallization texture is a retained deformation texture with an emerging Cube component.
文摘In this work,the micromechanical properties,crystallographic texture,welding residual stresses and their evolution after plastic strain were investigated in a Ti-6Al-4V alloy tungsten inert gas weld joint.It was found that the welding process affected the Young modulus and microhardness values in bothαandβphases in the different regions of the weld joint.The highest microhardness and Young modulus values of a phase were recorded in the heat-affected zone,whereas the highest values of these characteristics for theβphase were found in the fusion zone(FZ).The change in the micro mechanical properties was accompanied by a change in the crystallographic texture components of the dominant a phase from(0001)<10-10>and(11-20)<10-10>components in the base material to(10-10)<11-20>and(11-20)<3-302>components in the FZ.The introduction of tensile testing resulted in a continuous stress relaxation and improved the weld joint performances.
