The classification, characteristics and current situation of aluminum melt hydrogen-removal methods and technologies have been summarized. The latest studies and research results of aluminum melt degassing technology ...The classification, characteristics and current situation of aluminum melt hydrogen-removal methods and technologies have been summarized. The latest studies and research results of aluminum melt degassing technology have been summed up. The tendency and prospect of aluminum degassing technology was discussed.展开更多
Mg-content cored-wire was used to desulphurize and spheroidize ductile iron melt in industrial experiments. The optimal feeding speed and suitable treatment temperature were determined in the experiments. And cored-wi...Mg-content cored-wire was used to desulphurize and spheroidize ductile iron melt in industrial experiments. The optimal feeding speed and suitable treatment temperature were determined in the experiments. And cored-wire method and pouring method were compared. Conclusions have been drawn that, under these conditions in the experiments, the optimal feeding speed is 15m/min, treatment temperature should be as low as possible, 1400-1450℃ generally; and cored-wire method can act more effective in ductile iron melt desulphurization and spheroid than pouring method.展开更多
Electromagnetic separation of non-metallic inclusions from Al-Si melt is studied by theoretical analysis and experiments on self-designed electromagnetic separation apparatus. Metallographs and LECO Image Analysis Sy...Electromagnetic separation of non-metallic inclusions from Al-Si melt is studied by theoretical analysis and experiments on self-designed electromagnetic separation apparatus. Metallographs and LECO Image Analysis System were used to analyze the content of alumina in aluminum alloy before and after electromagnetic separation. It is seen that removal effciency increases with the increase of electromagnetic force (EMF) and diameter of inclusion particles while decreases with the increase of melt velocity and height of separator. All alumina particles with diamete of 14μm have been removed successfully from the melt.展开更多
文摘The classification, characteristics and current situation of aluminum melt hydrogen-removal methods and technologies have been summarized. The latest studies and research results of aluminum melt degassing technology have been summed up. The tendency and prospect of aluminum degassing technology was discussed.
基金the High Technology Research and Development Program of China(No.2002A4336072)
文摘Mg-content cored-wire was used to desulphurize and spheroidize ductile iron melt in industrial experiments. The optimal feeding speed and suitable treatment temperature were determined in the experiments. And cored-wire method and pouring method were compared. Conclusions have been drawn that, under these conditions in the experiments, the optimal feeding speed is 15m/min, treatment temperature should be as low as possible, 1400-1450℃ generally; and cored-wire method can act more effective in ductile iron melt desulphurization and spheroid than pouring method.
基金This work supported by the National Natural Science Foundation of China(Grant,No.59871029)the National Key Fundamental Research Project(973)(No.G1999064900)
文摘Electromagnetic separation of non-metallic inclusions from Al-Si melt is studied by theoretical analysis and experiments on self-designed electromagnetic separation apparatus. Metallographs and LECO Image Analysis System were used to analyze the content of alumina in aluminum alloy before and after electromagnetic separation. It is seen that removal effciency increases with the increase of electromagnetic force (EMF) and diameter of inclusion particles while decreases with the increase of melt velocity and height of separator. All alumina particles with diamete of 14μm have been removed successfully from the melt.