Several types of REBa2Cu3O7-x （REBCO, RE=Y, Ho etc.） films are prepared on single crystal substrate LaAIO3 by TFA-MOD method. The phase transformation and optimized growth conditions in the crystallization are studi...Several types of REBa2Cu3O7-x （REBCO, RE=Y, Ho etc.） films are prepared on single crystal substrate LaAIO3 by TFA-MOD method. The phase transformation and optimized growth conditions in the crystallization are studied. Compared with SmBCO and GdBCO, high quality YBCO and HoBCO films are relatively easy to produce. It is revealed that the YBCO grains can form at low temperatures such as 730 ℃ during the initial heating ramp. With a high heating rate of 20 K/min and a low oxygen pressure of 100 ppm, the optimum growth temperature is around 780℃, at which the films show a Jc value of 2.88 MMcm2. Further decrease of the heating rate may produce the highquality YBCO Film with a higher Jc of 3.65 MA/cm2. The temperature dependence of resistances in various magnetic fields up to 9 T shows that the present TFAMOD YBCO and HoBCO films have similar superonducting transition temperature and magnetotransport properties.展开更多
基金This work was supported by the National Natural Science Foundation of China under Grant No. 50672057, 50702033 and 10774098the National Science Foundation of China (973 Projects) under Grant No. 2006CB601005+1 种基金the Science and Technology Commission of Shanghai Municipality under Grant No. 0752nm017the Project Based Personnel Exchange Program between China and Germany under Grant No. [2006] 3139.
文摘Several types of REBa2Cu3O7-x （REBCO, RE=Y, Ho etc.） films are prepared on single crystal substrate LaAIO3 by TFA-MOD method. The phase transformation and optimized growth conditions in the crystallization are studied. Compared with SmBCO and GdBCO, high quality YBCO and HoBCO films are relatively easy to produce. It is revealed that the YBCO grains can form at low temperatures such as 730 ℃ during the initial heating ramp. With a high heating rate of 20 K/min and a low oxygen pressure of 100 ppm, the optimum growth temperature is around 780℃, at which the films show a Jc value of 2.88 MMcm2. Further decrease of the heating rate may produce the highquality YBCO Film with a higher Jc of 3.65 MA/cm2. The temperature dependence of resistances in various magnetic fields up to 9 T shows that the present TFAMOD YBCO and HoBCO films have similar superonducting transition temperature and magnetotransport properties.