High-pressure torsion(HPT)processing under a pressure of 6.0 GPa was applied to Ti29.7Ni50.3Hf20(at.%)alloy.Two types of structure were observed after HPT with 3 revolutions:first one is the mixture of amorphous phase...High-pressure torsion(HPT)processing under a pressure of 6.0 GPa was applied to Ti29.7Ni50.3Hf20(at.%)alloy.Two types of structure were observed after HPT with 3 revolutions:first one is the mixture of amorphous phase and retained nanocrystalline;second is the alternating bands of amorphous phase and high defect density crystalline.As a result,post deformation annealing(PDA)at 500-700℃leads to the non-uniform distribution of martensite and parent phase grains.The grains of martensite are twice larger compared to that of parent phase.The nanocrystalline and ultrafine grains form after annealing at 500-600℃and 700℃,respectively.The twinning mechanism does not change with the reduction of martensitic grains up to^35 nm.The relationship between strength and grain size in Ti29.7Ni50.3Hf20 alloy obeys the classical Hall-Petch relationship with a coefficient of 10.80±0.39 GPa nm^1/2.展开更多
Precipitate hardening is the most easiest and effective way to enhance strain recovery properties in NiTiHf high-temperature shape memory alloys.This paper discusses the precipitation,coarsening and age hardening of H...Precipitate hardening is the most easiest and effective way to enhance strain recovery properties in NiTiHf high-temperature shape memory alloys.This paper discusses the precipitation,coarsening and age hardening of H-phase precipitates in Ni_(50)Ti_(30)Hf_(20)alloy during isothermal aging at temperatures between 450℃and 650℃for time to 75 h.The H-phase mean size and volume fraction were determined using transmission electron microscopy.Precipitation kinetics was analyzed using the Johnson-Mehl-Avrami-Kolmogorov equation and an Arrhenius type law.From these analyses,a Time-Temperature-Transformation diagram was constructed.The evolution of H-phase size suggests classical matrix diffusion limited Lifshitz-Slyozov-Wagner coarsening for all considered temperatures.The coarsening rate constants of H-phase precipitation have been determined using a modified coarsening rate equation for nondilute solutions.Critical size of H-phase precipitates for breaking down the precipitate/matrix interface coherency was estimated through a combination of age hardening and precipitate size evolution data.Moreover,time-temperature-hardness diagram was constructed from the precipitation and coarsening kinetics and age hardening of H-phase precipitates in Ni_(50)Ti_(30)Hf_(20)alloy.展开更多
基金supported by National Key R&D Program of China[grant number 2017YFE0123500]National Natural Science Foundation of China[grant number 51971072,51671064]+2 种基金the Fundamental Research Funds for the Central University[grant number HEUCFG201836]the support from the RFBR-CNPq-DST research project№19-58-80018the support in part from the Russian Foundation for Basic Research(project No.20-03-00614)。
文摘High-pressure torsion(HPT)processing under a pressure of 6.0 GPa was applied to Ti29.7Ni50.3Hf20(at.%)alloy.Two types of structure were observed after HPT with 3 revolutions:first one is the mixture of amorphous phase and retained nanocrystalline;second is the alternating bands of amorphous phase and high defect density crystalline.As a result,post deformation annealing(PDA)at 500-700℃leads to the non-uniform distribution of martensite and parent phase grains.The grains of martensite are twice larger compared to that of parent phase.The nanocrystalline and ultrafine grains form after annealing at 500-600℃and 700℃,respectively.The twinning mechanism does not change with the reduction of martensitic grains up to^35 nm.The relationship between strength and grain size in Ti29.7Ni50.3Hf20 alloy obeys the classical Hall-Petch relationship with a coefficient of 10.80±0.39 GPa nm^1/2.
基金supported by the National Natural Sci-ence Foundation of China(Nos.52050410340 and 51971072)the Fundamental Research Funds for the Central University(No.3072021CFJ1002).
文摘Precipitate hardening is the most easiest and effective way to enhance strain recovery properties in NiTiHf high-temperature shape memory alloys.This paper discusses the precipitation,coarsening and age hardening of H-phase precipitates in Ni_(50)Ti_(30)Hf_(20)alloy during isothermal aging at temperatures between 450℃and 650℃for time to 75 h.The H-phase mean size and volume fraction were determined using transmission electron microscopy.Precipitation kinetics was analyzed using the Johnson-Mehl-Avrami-Kolmogorov equation and an Arrhenius type law.From these analyses,a Time-Temperature-Transformation diagram was constructed.The evolution of H-phase size suggests classical matrix diffusion limited Lifshitz-Slyozov-Wagner coarsening for all considered temperatures.The coarsening rate constants of H-phase precipitation have been determined using a modified coarsening rate equation for nondilute solutions.Critical size of H-phase precipitates for breaking down the precipitate/matrix interface coherency was estimated through a combination of age hardening and precipitate size evolution data.Moreover,time-temperature-hardness diagram was constructed from the precipitation and coarsening kinetics and age hardening of H-phase precipitates in Ni_(50)Ti_(30)Hf_(20)alloy.